- 密度 [g/cm3]: 1.2
- 吸水率 [%]: 4.0
- 弯曲强度 [MPa]: 42.0
- 热变形温度 [℃]: 195.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | |
| Water Absorption | 4.0 % | 4.0 % | Saturation in water |
| Water Absorption at Saturation | 4.0 % | 4.0 % | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 42.0 MPa | 6090 psi | |
| Elongation at Break | 4.0 % | 4.0 % | |
| Tensile Modulus | 1.30 GPa | 189 ksi | |
| Charpy Impact Unnotched | 2.80 J/cm² | 13.3 ft-lb/in² | |
| Tensile Creep Modulus, 1 hour | 1250 MPa | 181000 psi | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 7.00e+13 ohm-cm | 7.00e+13 ohm-cm | |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | |
| Dielectric Strength | 15.0 kV/mm | 381 kV/in | |
| Comparative Tracking Index | 600 V | 600 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 140 µm/m-°C @Temperature 20.0 °C | 77.8 µin/in-°F @Temperature 68.0 °F | in flow direction |
| CTE, linear, Transverse to Flow | 140 µm/m-°C @Temperature 20.0 °C | 77.8 µin/in-°F @Temperature 68.0 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 195 °C | 383 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 136 °C | 277 °F | |
| Vicat Softening Point | 245 °C | 473 °F | |