- 弯曲强度 [MPa]: 33.61
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.80 - 1.90 g/cc | 1.80 - 1.90 g/cc | ASTM D792-66 | ||
| Brookfield Viscosity | 2075 cP | 2075 cP | #3 spindle @ 20 rpm; ASTM D2393 | ||
| Linear Mold Shrinkage | 0.00080 cm/cm | 0.00080 in/in | ASTM D2566-69 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 85 @Temperature 23.9 °C | 85 @Temperature 75.0 °F | ASTM D2240 | ||
| Tensile Strength, Ultimate | 33.61 MPa | 4875 psi | ASTM D638 | ||
| Flexural Strength | 43.1 MPa | 6250 psi | |||
| Compressive Strength | 66.2 MPa | 9600 psi | ASTM D695 | ||
| Thermal Properties | Metric | English | Comments | ||
| Heat Distortion Temperature | 78.9 °C | 174 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 60.0 - 120 min @Temperature 25.0 °C | 1.00 - 2.00 hour @Temperature 77.0 °F | demold time | ||
| Pot Life | 5.0 - 6.0 min @Temperature 25.0 °C | 5.0 - 6.0 min @Temperature 77.0 °F | 1 lb. mass | ||
| Descriptive Properties | |||||
| Mix Ratio | 1:1 by weight or volume | ||||
| Wear Resistance (Tabor Method) | Very Good | ||||