- 弯曲强度 [MPa]: 27.9
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.75 - 1.85 g/cc | 1.75 - 1.85 g/cc | |||
| Brookfield Viscosity | 2250 cP @Temperature 23.9 °C | 2250 cP @Temperature 75.0 °F | 1 minute, #3 spindle @ 20 rpm | ||
| Linear Mold Shrinkage | 0.00070 cm/cm | 0.00070 in/in | ASTM D2566-69 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 83 @Temperature 23.9 °C | 83 @Temperature 75.0 °F | |||
| Tensile Strength, Ultimate | 27.90 MPa | 4046 psi | ASTM D638 | ||
| Flexural Strength | 45.9 MPa | 6650 psi | ASTM D790 | ||
| Compressive Strength | 67.2 MPa | 9750 psi | ASTM D695 | ||
| Thermal Properties | Metric | English | Comments | ||
| Heat Distortion Temperature | 81.7 °C | 179 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 90.0 - 120 min @Temperature 24.0 °C | 1.50 - 2.00 hour @Temperature 75.2 °F | demold time | ||
| Pot Life | 6.0 - 7.0 min @Temperature 24.0 °C | 6.0 - 7.0 min @Temperature 75.2 °F | 1 lb. mass | ||
| Descriptive Properties | |||||
| Mix Ratio | 1:1 by weight or volume | ||||