- 弯曲强度 [MPa]: 3.38
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.03 g/cc | 1.03 g/cc | |||
| Brookfield Viscosity | 850 cP @Temperature 25.0 °C | 850 cP @Temperature 77.0 °F | |||
| Linear Mold Shrinkage | 0.00050 cm/cm | 0.00050 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 38 - 42 | 38 - 42 | |||
| Tensile Strength, Ultimate | 3.38 MPa | 490 psi | |||
| Elongation at Break | 800 % | 800 % | |||
| Tear Strength | 35.1 kN/m | 200 pli | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 720 - 960 min @Temperature 24.0 °C | 12.0 - 16.0 hour @Temperature 75.2 °F | demold time | ||
| 1440 min @Temperature 24.0 °C | 24.0 hour @Temperature 75.2 °F | full cure | |||
| Pot Life | 30 min @Temperature 25.0 °C | 30 min @Temperature 77.0 °F | work life | ||
| 45 min @Temperature 25.0 °C | 45 min @Temperature 77.0 °F | gel time (180g) | |||
| Descriptive Properties | |||||
| Mix Ratio | 100:90 by weight (resin/hardener) | ||||