- 弯曲强度 [MPa]: 40.0
- 弯曲模量 [MPa]: 1.45
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.07 g/cc | 1.07 g/cc | |||
| Brookfield Viscosity | 640 cP | 640 cP | Part B | ||
| 36 cP @Temperature 23.9 °C | 36 cP @Temperature 75.0 °F | Part A | |||
| 230 cP @Temperature 23.9 °C | 230 cP @Temperature 75.0 °F | Mixed | |||
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | ASTM D2566 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 81 - 85 @Temperature 23.9 °C | 81 - 85 @Temperature 75.0 °F | |||
| Tensile Strength, Ultimate | 40.0 MPa | 5800 psi | ASTM D638 | ||
| Elongation at Break | 2.4 % | 2.4 % | ASTM D638 | ||
| Flexural Strength | 52.7 MPa | 7650 psi | ASTM D790 | ||
| Flexural Modulus | 1.45 GPa | 210 ksi | ASTM D790 | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 60.0 - 120 min @Temperature 24.0 °C | 1.00 - 2.00 hour @Temperature 75.2 °F | demold time | ||
| 10080 min @Temperature 24.0 °C | 168.0 hour @Temperature 75.2 °F | full cure | |||
| Pot Life | 8.0 - 10 min @Temperature 24.0 °C | 8.0 - 10 min @Temperature 75.2 °F | 1 lb. mass | ||
| Descriptive Properties | |||||
| Mix Ratio | 100:80 by weight, 100:87 by volume, resin/harder | ||||