- 拉伸强度 [MPa]: 1717.0
- 断裂伸长率 [%]: 1558
- 弯曲模量 [MPa]: 125.5
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 1717 MPa | 249000 psi | Room temperature |
| 1482 MPa @Temperature 71.0 °C | 214900 psi @Temperature 160 °F | 1/2 hr | |
| Tensile Modulus | 110.3 GPa | 16000 ksi | Room temperature |
| 108.9 GPa @Temperature 71.0 °C | 15790 ksi @Temperature 160 °F | 1/2 hr | |
| Flexural Yield Strength | 1558 MPa | 226000 psi | Room temperature |
| 1289 MPa @Temperature 71.0 °C | 187000 psi @Temperature 160 °F | 1/2 hr | |
| Flexural Modulus | 125.5 GPa | 18200 ksi | Room temperature |
| 124.8 GPa @Temperature 71.0 °C | 18100 ksi @Temperature 160 °F | 1/2 hr | |
| Compressive Yield Strength | 1303 MPa | 189000 psi | Room temperature |
| 1158 MPa @Temperature 71.0 °C | 168000 psi @Temperature 160 °F | 1/2 hr | |
| Compressive Modulus | 117.9 GPa | 17100 ksi | Room temperature |
| 112.4 GPa @Temperature 71.0 °C | 16300 ksi @Temperature 160 °F | 1/2 hr | |
| Shear Strength | 86.9 MPa | 12600 psi | Short Beam, Room temperature |
| 69.6 MPa @Temperature 71.0 °C | 10100 psi @Temperature 160 °F | Short Beam, 1/2 hr | |