- 密度 [g/cm3]: 1.26
- 拉伸强度 [MPa]: 400.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.26 g/cc | 0.0455 lb/in³ | Resin Density | ||
| 2.10 g/cc | 0.0759 lb/in³ | Fibre Density | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 400 MPa | 58000 psi | 90º, RT, Dry; EN2561 | ||
| 320 MPa @Temperature 130 °C | 46400 psi @Temperature 266 °F | 90º, Wet; EN2561 | |||
| 370 MPa @Temperature 23.0 °C | 53700 psi @Temperature 73.4 °F | 90º, Wet; EN2561 | |||
| Tensile Modulus | 38.0 GPa | 5510 ksi | 90º, RT, Dry; EN2561 | ||
| 37.0 GPa @Temperature 23.0 °C | 5370 ksi @Temperature 73.4 °F | 90º, Wet; EN2561 | |||
| 37.0 GPa @Temperature 130 °C | 5370 ksi @Temperature 266 °F | 90º, Wet; EN2561 | |||
| Compressive Yield Strength | 650 MPa | 94300 psi | 90º, RT, Dry; EN2850 Type B | ||
| 390 MPa @Temperature 130 °C | 56600 psi @Temperature 266 °F | 90º, Wet; EN2850 Type B | |||
| 590 MPa @Temperature 23.0 °C | 85600 psi @Temperature 73.4 °F | 90º, Wet; EN2850 Type B | |||
| Compressive Modulus | 37.0 GPa | 5370 ksi | 90º, RT, Dry; EN2850 Type B | ||
| 36.0 GPa @Temperature 130 °C | 5220 ksi @Temperature 266 °F | 90º, Wet; EN2850 Type B | |||
| 38.0 GPa @Temperature 23.0 °C | 5510 ksi @Temperature 73.4 °F | 90º, Wet; EN2850 Type B | |||
| Shear Modulus | 3.50 GPa | 508 ksi | In-Plane, RT, Dry; EN6031 | ||
| 2.40 GPa @Temperature 130 °C | 348 ksi @Temperature 266 °F | In-Plane, Wet; EN6031 | |||
| Shear Strength | 68.0 MPa | 9860 psi | 90º, ILSS Short Beam, RT, Dry; EN2563 | ||
| 79.0 MPa | 11500 psi | In-Plane, RT, Dry; EN6031 | |||
| 31.0 MPa @Temperature 150 °C | 4500 psi @Temperature 302 °F | 90º, ILSS Short Beam, Wet; EN2563 | |||
| 34.0 MPa @Temperature 130 °C | 4930 psi @Temperature 266 °F | 90º, ILSS Short Beam, Wet; EN2563 | |||
| 48.0 MPa @Temperature 130 °C | 6960 psi @Temperature 266 °F | In-Plane, Wet; EN6031 | |||
| 54.0 MPa @Temperature 100 °C | 7830 psi @Temperature 212 °F | In-Plane, Wet; EN6031 | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 120 - 130 °C | 248 - 266 °F | Epoxy Matrix Limit | ||
| Processing Properties | Metric | English | Comments | ||
| Shelf Life | 12.0 Month @Temperature -18.0 °C | 12.0 Month @Temperature -0.400 °F | |||
| Descriptive Properties | |||||
| Cured Thickness per Ply (cm) | 0.021 | ||||
| Fiber Volume (%) | 42 | ||||