Hexcel® HexPly® M42 180°C (350°F) Curing Epoxy Matrix, 50%/G939 HS Carbon物性表参数

Hexcel® HexPly® M42 180°C (350°F) Curing Epoxy Matrix, 50%/G939 HS Carbon

Hexcel® HexPly® M42 180°C (350°F) Curing Epoxy Matrix, 50%/G939 HS Carbon 物性表: Hexcel® HexPly® M42 180°C (350°F) Curing Epoxy Matrix, 50%/G939 HS Carbon物性表及特性介绍,Hexcel® HexPly® M42 180°C (350°F) Curing Epoxy Matrix, 50%/G939 HS Carbon注塑参数详情,如需Hexcel® HexPly® M42 180°C (350°F) Curing Epoxy Matrix, 50%/G939 HS Carbon下载, 可到相关下载区下载

密度 [g/cm3]: 1.26
拉伸强度 [MPa]: 850.0

Physical Properties	Metric	English	Comments

Density	1.26 g/cc	0.0455 lb/in³	Resin Density
	1.78 g/cc	0.0643 lb/in³	Fibre Density

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	850 MPa	123000 psi	90º, RT, Dry; EN2561
	750 MPa @Temperature 135 °C	109000 psi @Temperature 275 °F	90º, Wet; EN2561
Tensile Modulus	62.8 GPa	9110 ksi	90º, RT, Dry; EN2561
	60.0 GPa @Temperature 135 °C	8700 ksi @Temperature 275 °F	90º, Wet; EN2561
Compressive Yield Strength	730 MPa	106000 psi	90º, RT, Dry; EN2850 Type B
	530 MPa @Temperature 135 °C	76900 psi @Temperature 275 °F	90º, Wet; EN2850 Type B
Shear Strength	65.0 MPa	9430 psi	0º, ILSS Short Beam, RT, Dry; EN2563
	35.0 MPa @Temperature 135 °C	5080 psi @Temperature 275 °F	0º, ILSS Short Beam, Wet; EN2563
	49.0 MPa @Temperature 120 °C	7110 psi @Temperature 248 °F	0º, ILSS Short Beam, Dry; EN2563

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	120 - 130 °C	248 - 266 °F	Epoxy Matrix Limit

Processing Properties	Metric	English	Comments
Shelf Life	12.0 Month @Temperature -18.0 °C	12.0 Month @Temperature -0.400 °F

Descriptive Properties
Cured Thickness per Ply (cm)	0.022
Fiber Volume (%)	55

关键词:
供应
热固性复合材料
Hexcel® HexPly® M42 180°C (350°F) Curing Epoxy Matrix
50%/G939 HS Carbon

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-37684.html

免责声明: 本文 Hexcel® HexPly® M42 180°C (350°F) Curing Epoxy Matrix, 50%/G939 HS Carbon 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络