- 拉伸强度 [MPa]: 920.0
- 断裂伸长率 [%]: 935
- 弯曲模量 [MPa]: 40.0
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 920 MPa @Temperature 23.0 °C | 133000 psi @Temperature 73.4 °F | 0º, Conditioning: 23°C; ASTM D3039 |
| Tensile Modulus | 60.0 GPa @Temperature 23.0 °C | 8700 ksi @Temperature 73.4 °F | 0º, Conditioning: 23°C; ASTM D3039 |
| Flexural Yield Strength | 935 MPa @Temperature 90.0 °C | 136000 psi @Temperature 194 °F | 0º, Conditioning: 23°C; ASTM D790 |
| 950 MPa @Temperature 23.0 °C | 138000 psi @Temperature 73.4 °F | 0º, Conditioning: 23°C; ASTM D790 | |
| Flexural Modulus | 40.0 GPa @Temperature 90.0 °C | 5800 ksi @Temperature 194 °F | 0º, Conditioning: 23°C; ASTM D790 |
| 43.0 GPa @Temperature 23.0 °C | 6240 ksi @Temperature 73.4 °F | 0º, Conditioning: 23°C; ASTM D790 | |
| Compressive Yield Strength | 537 MPa @Temperature 90.0 °C | 77900 psi @Temperature 194 °F | 0º, Conditioning: 23°C; ASTM D965 |
| 715 MPa @Temperature 23.0 °C | 104000 psi @Temperature 73.4 °F | 0º, Conditioning: 23°C; ASTM D965 | |
| Shear Strength | 39.0 MPa @Temperature 60.0 °C | 5660 psi @Temperature 140 °F | 0º Interlaminar Shear, Conditioning: 60°C-90%RH; ASTM D2344 |
| 57.0 MPa @Temperature 90.0 °C | 8270 psi @Temperature 194 °F | 0º Interlaminar Shear, Conditioning: 23°C; ASTM D2344 | |
| 80.0 MPa @Temperature 23.0 °C | 11600 psi @Temperature 73.4 °F | 0º Interlaminar Shear, Conditioning: 23°C; ASTM D2344 | |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 120 - 130 °C | 248 - 266 °F | Epoxy Matrix Limit |
| Processing Properties | Metric | English | Comments |
| Shelf Life | 12.0 Month @Temperature -18.0 °C | 12.0 Month @Temperature -0.400 °F | |