- 弯曲模量 [MPa]: 8.96
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Viscosity | 0.0500 cP @Temperature 120 °C | 0.0500 cP @Temperature 248 °F | Rheology, 2°C/min | ||
| 0.0700 cP @Temperature 80.0 °C | 0.0700 cP @Temperature 176 °F | Rheology, 2°C/min | |||
| 1.00 cP @Temperature 40.0 °C | 1.00 cP @Temperature 104 °F | Rheology, 2°C/min | |||
| 100 cP @Temperature 140 °C | 100 cP @Temperature 284 °F | Rheology, 2°C/min | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength | 46.2 MPa | 6700 psi | 90°; ASTM D3039 | ||
| 2560 MPa | 371000 psi | 0°; ASTM D3039 | |||
| Tensile Modulus | 9.65 GPa | 1400 ksi | 90°; ASTM D3039 | ||
| 152 GPa | 22000 ksi | 0°; ASTM D3039 | |||
| Flexural Strength | 113 MPa | 16400 psi | 90°; ASTM D790 | ||
| 1830 MPa | 265000 psi | 0°; ASTM D790 | |||
| Flexural Modulus | 8.96 GPa | 1300 ksi | 90°; ASTM D790 | ||
| 176 GPa | 25500 ksi | 0°; ASTM D790 | |||
| Compressive Strength | 224 MPa | 32500 psi | 90°; SACMA SRM 1R-94 | ||
| 1170 MPa | 170000 psi | 0°; SACMA SRM 1R-94 | |||
| Compressive Modulus | 10.3 GPa | 1500 ksi | 90°; SACMA SRM 1R-94 | ||
| 141 GPa | 20400 ksi | 0°; SACMA SRM 1R-94 | |||
| Poissons Ratio | 0.340 | 0.340 | ASTM D3039 | ||
| Shear Strength | 82.7 MPa | 12000 psi | Short Beam; ASTM D2344 | ||
| Thermal Properties | Metric | English | Comments | ||
| Glass Transition Temp, Tg | 138 °C | 280 °F | ASTM D702807 | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 30.0 min @Temperature 137.8 °C | 0.500 hour @Temperature 280.0 °F | |||
| 120 min @Temperature 121.1 °C | 2.00 hour @Temperature 250.0 °F | ||||
| 120 min @Temperature 121 °C | 2.00 hour @Temperature 250 °F | 80 psi | |||
| 240 min @Temperature 104.4 °C | 4.00 hour @Temperature 219.9 °F | ||||
| 360 min @Temperature 93.3 °C | 6.00 hour @Temperature 200 °F | ||||
| 720 min @Temperature 82.2 °C | 12.0 hour @Temperature 180 °F | ||||
| Gel Time | 5.00 min @Temperature 137.8 °C | 5.00 min @Temperature 280.0 °F | |||
| 13.0 min @Temperature 121.1 °C | 13.0 min @Temperature 250.0 °F | ||||
| 33.0 min @Temperature 104.4 °C | 33.0 min @Temperature 219.9 °F | ||||
| 68.0 min @Temperature 93.3 °C | 68.0 min @Temperature 200 °F | ||||
| 168 min @Temperature 82.2 °C | 168 min @Temperature 180 °F | ||||
| Shelf Life | 12.0 Month @Temperature -17.8 °C | 12.0 Month @Temperature 0.000 °F | |||
| Descriptive Properties | |||||
| GIc Strain Release Energy | 3.0 in-lb/in² | ASTM D5528-07 | |||