- 弯曲模量 [MPa]: 56.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Viscosity | 0.0500 cP @Temperature 120 °C | 0.0500 cP @Temperature 248 °F | Rheology, 2°C/min | ||
| 0.0700 cP @Temperature 80.0 °C | 0.0700 cP @Temperature 176 °F | Rheology, 2°C/min | |||
| 1.00 cP @Temperature 40.0 °C | 1.00 cP @Temperature 104 °F | Rheology, 2°C/min | |||
| 100 cP @Temperature 140 °C | 100 cP @Temperature 284 °F | Rheology, 2°C/min | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength | 758 MPa | 110000 psi | with 3K Plain Weave AS-2 Carbon Fiber; ASTM D638 | ||
| 889 MPa | 129000 psi | with 3K Resin with 3K Twill TR30 Carbon Fiber; ASTM D638 | |||
| Tensile Modulus | 64.9 GPa | 9410 ksi | with 3K Resin with 3K Twill TR30 Carbon Fiber; ASTM D638 | ||
| 71.4 GPa | 10400 ksi | with 3K Plain Weave AS-2 Carbon Fiber; ASTM D638 | |||
| Flexural Strength | 807 MPa | 117000 psi | with 3K Plain Weave AS-2 Carbon Fiber; ASTM D790 | ||
| 1010 MPa | 146000 psi | with 3K Resin with 3K Twill TR30 Carbon Fiber; ASTM D790 | |||
| Flexural Modulus | 56.0 GPa | 8120 ksi | with 3K Plain Weave AS-2 Carbon Fiber; ASTM D790 | ||
| 56.7 GPa | 8220 ksi | with 3K Resin with 3K Twill TR30 Carbon Fiber; ASTM D790 | |||
| Compressive Strength | 456 MPa | 66100 psi | with 3K Plain Weave AS-2 Carbon Fiber; ASTM D695 | ||
| 601 MPa | 87200 psi | with 3K Resin with 3K Twill TR30 Carbon Fiber; ASTM D695 | |||
| Shear Strength | 71.4 MPa | 10400 psi | Short Beam, with 3K Plain Weave AS-2 Carbon Fiber; ASTM D2344 | ||
| 74.39 MPa | 10790 psi | Short Beam, with 3K Resin with 3K Twill TR30 Carbon Fiber; ASTM D2344 | |||
| Thermal Properties | Metric | English | Comments | ||
| Glass Transition Temp, Tg | 112.4 °C | 234.3 °F | with 3K Resin with 3K Twill TR30 Carbon Fiber; ASTM D7028-07 | ||
| 125 °C | 258 °F | with 3K Plain Weave AS-2 Carbon Fiber; ASTM D7028-07 | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 30.0 min @Temperature 137.8 °C | 0.500 hour @Temperature 280.0 °F | |||
| 120 min @Temperature 121.1 °C | 2.00 hour @Temperature 250.0 °F | ||||
| 120 min @Temperature 121 °C | 2.00 hour @Temperature 250 °F | 80 psi | |||
| 240 min @Temperature 104.4 °C | 4.00 hour @Temperature 219.9 °F | ||||
| 360 min @Temperature 93.3 °C | 6.00 hour @Temperature 200 °F | ||||
| 720 min @Temperature 82.2 °C | 12.0 hour @Temperature 180 °F | ||||
| Gel Time | 5.00 min @Temperature 137.8 °C | 5.00 min @Temperature 280.0 °F | |||
| 13.0 min @Temperature 121.1 °C | 13.0 min @Temperature 250.0 °F | ||||
| 33.0 min @Temperature 104.4 °C | 33.0 min @Temperature 219.9 °F | ||||
| 68.0 min @Temperature 93.3 °C | 68.0 min @Temperature 200 °F | ||||
| 168 min @Temperature 82.2 °C | 168 min @Temperature 180 °F | ||||
| Shelf Life | 12.0 Month @Temperature -17.8 °C | 12.0 Month @Temperature 0.000 °F | |||
| Descriptive Properties | |||||
| GIC Mode I Energy | 4.2 in-lb/in² | ASTM D5528-07, with 3K Twill TR30 Carbon Fiber | |||
| 4.8 in-lb/in² | ASTM D5528-07, with 3K Plain Weave AS-2 Carbon Fiber | ||||