- 熔体流动速率 [g/10min]: 3.2
- 密度 [g/cm3]: 1.17
- 吸水率 [%]: 0.06
- 缺口冲击强度: 0.427
- 拉伸强度 [MPa]: 48.0
- 断裂伸长率 [%]: 85.0
- 弯曲强度 [MPa]: 45.0
- 弯曲模量 [MPa]: 1.72
- 硬度: 95.0
- 热变形温度 [℃]: 108.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.17 - 1.60 g/cc | 0.0423 - 0.0578 lb/in³ | Average value: 1.39 g/cc Grade Count:42 |
| Water Absorption | 0.0600 - 0.400 % | 0.0600 - 0.400 % | Average value: 0.206 % Grade Count:9 |
| Moisture Absorption at Equilibrium | 0.0800 - 0.160 % | 0.0800 - 0.160 % | Average value: 0.120 % Grade Count:15 |
| Water Absorption at Saturation | 0.100 - 0.500 % | 0.100 - 0.500 % | Average value: 0.349 % Grade Count:10 |
| Maximum Moisture Content | 0.0200 | 0.0200 | Average value: 0.0200 Grade Count:3 |
| Linear Mold Shrinkage | 0.00100 - 0.0100 cm/cm | 0.00100 - 0.0100 in/in | Average value: 0.00488 cm/cm Grade Count:33 |
| Linear Mold Shrinkage, Transverse | 0.00400 - 0.00900 cm/cm | 0.00400 - 0.00900 in/in | Average value: 0.00590 cm/cm Grade Count:11 |
| Melt Flow | 3.20 - 56.0 g/10 min | 3.20 - 56.0 g/10 min | Average value: 25.3 g/10 min Grade Count:24 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 95.0 - 119 | 95.0 - 119 | Average value: 113 Grade Count:10 |
| Hardness, H358/30 | 95.0 - 115 MPa | 13800 - 16700 psi | Average value: 104 MPa Grade Count:4 |
| Tensile Strength, Ultimate | 45.0 - 132 MPa | 6530 - 19100 psi | Average value: 90.4 MPa Grade Count:29 |
| Tensile Strength, Yield | 48.0 - 114 MPa | 6960 - 16500 psi | Average value: 88.2 MPa Grade Count:22 |
| Elongation at Break | 1.00 - 200 % | 1.00 - 200 % | Average value: 11.3 % Grade Count:39 |
| Elongation at Yield | 1.00 - 3.60 % | 1.00 - 3.60 % | Average value: 2.29 % Grade Count:9 |
| Modulus of Elasticity | 2.80 - 12.8 GPa | 406 - 1860 ksi | Average value: 7.05 GPa Grade Count:21 |
| Flexural Yield Strength | 85.0 - 196 MPa | 12300 - 28400 psi | Average value: 145 MPa Grade Count:31 |
| Flexural Modulus | 1.72 - 9.06 GPa | 250 - 1310 ksi | Average value: 5.48 GPa Grade Count:36 |
| Izod Impact, Notched | 0.427 - 10.8 J/cm | 0.800 - 20.2 ft-lb/in | Average value: 1.83 J/cm Grade Count:26 |
| 0.600 - 1.12 J/cm @Temperature -30.0 - -30.0 °C | 1.12 - 2.10 ft-lb/in @Temperature -22.0 - -22.0 °F | Average value: 0.883 J/cm Grade Count:6 | |
| 1.01 - 1.07 J/cm @Temperature -20.0 - -20.0 °C | 1.89 - 2.00 ft-lb/in @Temperature -4.00 - -4.00 °F | Average value: 0.883 J/cm Grade Count:2 | |
| 1.01 - 1.07 J/cm @Thickness 3.18 - 3.18 mm | 1.89 - 2.00 ft-lb/in @Thickness 0.125 - 0.125 in | Average value: 0.883 J/cm Grade Count:2 | |
| Izod Impact, Unnotched | 5.93 - 9.50 J/cm | 11.1 - 17.8 ft-lb/in | Average value: 6.83 J/cm Grade Count:7 |
| Izod Impact, Notched (ISO) | 3.00 - 10.0 kJ/m² | 1.43 - 4.76 ft-lb/in² | Average value: 6.86 kJ/m² Grade Count:14 |
| 3.00 - 11.0 kJ/m² @Temperature -30.0 - 0.000 °C | 1.43 - 5.23 ft-lb/in² @Temperature -22.0 - 32.0 °F | Average value: 5.71 kJ/m² Grade Count:13 | |
| Izod Impact, Unnotched (ISO) | 25.0 - 55.0 kJ/m² | 11.9 - 26.2 ft-lb/in² | Average value: 40.2 kJ/m² Grade Count:6 |
| 27.0 - 80.0 kJ/m² @Temperature -30.0 - -30.0 °C | 12.8 - 38.1 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 46.8 kJ/m² Grade Count:5 | |
| Charpy Impact Unnotched | 2.70 - 5.50 J/cm² | 12.8 - 26.2 ft-lb/in² | Average value: 4.17 J/cm² Grade Count:10 |
| 2.20 - 5.50 J/cm² @Temperature -30.0 - -30.0 °C | 10.5 - 26.2 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 3.64 J/cm² Grade Count:5 | |
| Charpy Impact, Notched | 0.400 - 2.10 J/cm² | 1.90 - 9.99 ft-lb/in² | Average value: 1.28 J/cm² Grade Count:12 |
| 0.300 - 1.00 J/cm² @Temperature -30.0 - -30.0 °C | 1.43 - 4.76 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 0.675 J/cm² Grade Count:4 | |
| Dart Drop, Total Energy | 5.00 - 17.0 J | 3.69 - 12.5 ft-lb | Average value: 9.11 J Grade Count:7 |
| 3.00 - 7.00 J @Temperature -30.0 - -20.0 °C | 2.21 - 5.16 ft-lb @Temperature -22.0 - -4.00 °F | Average value: 3.75 J Grade Count:3 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+14 - 1.00e+16 ohm-cm | 1.00e+14 - 1.00e+16 ohm-cm | Average value: 3.39e+15 ohm-cm Grade Count:8 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | Average value: 1.00e+15 ohm Grade Count:6 |
| Dielectric Constant | 2.90 - 4.00 | 2.90 - 4.00 | Average value: 3.45 Grade Count:9 |
| Dielectric Strength | 14.0 - 34.0 kV/mm | 356 - 864 kV/in | Average value: 22.2 kV/mm Grade Count:9 |
| Dissipation Factor | 0.00100 - 0.0200 | 0.00100 - 0.0200 | Average value: 0.00967 Grade Count:6 |
| Arc Resistance | 120 - 180 sec | 120 - 180 sec | Average value: 130 sec Grade Count:3 |
| Comparative Tracking Index | 100 - 400 V | 100 - 400 V | Average value: 194 V Grade Count:6 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 21.0 - 450 µm/m-°C | 11.7 - 250 µin/in-°F | Average value: 64.3 µm/m-°C Grade Count:19 |
| 19.8 - 19.8 µm/m-°C @Temperature 60.0 - 138 °C | 11.0 - 11.0 µin/in-°F @Temperature 140 - 280 °F | Average value: 19.8 µm/m-°C Grade Count:1 | |
| CTE, linear, Transverse to Flow | 30.0 - 110 µm/m-°C | 16.7 - 61.1 µin/in-°F | Average value: 78.9 µm/m-°C Grade Count:15 |
| Thermal Conductivity | 0.180 - 0.190 W/m-K | 1.25 - 1.32 BTU-in/hr-ft²-°F | Average value: 0.187 W/m-K Grade Count:3 |
| Melting Point | 220 - 225 °C | 428 - 437 °F | Average value: 224 °C Grade Count:7 |
| Deflection Temperature at 0.46 MPa (66 psi) | 108 - 212 °C | 226 - 414 °F | Average value: 162 °C Grade Count:26 |
| Deflection Temperature at 1.8 MPa (264 psi) | 62.8 - 195 °C | 145 - 383 °F | Average value: 135 °C Grade Count:41 |
| Vicat Softening Point | 121 - 212 °C | 250 - 414 °F | Average value: 154 °C Grade Count:16 |
| UL RTI, Electrical | 75.0 - 140 °C | 167 - 284 °F | Average value: 108 °C Grade Count:4 |
| UL RTI, Mechanical with Impact | 75.0 - 130 °C | 167 - 266 °F | Average value: 103 °C Grade Count:4 |
| UL RTI, Mechanical without Impact | 75.0 - 140 °C | 167 - 284 °F | Average value: 108 °C Grade Count:4 |
| Flammability, UL94 | HB - 5VA | HB - 5VA | Grade Count:19 |
| Glow Wire Test | 750 - 850 °C | 1380 - 1560 °F | Average value: 800 °C Grade Count:3 |
| Processing Properties | Metric | English | Comments |
| Nozzle Temperature | 245 - 279 °C | 473 - 535 °F | Average value: 258 °C Grade Count:5 |
| Melt Temperature | 225 - 282 °C | 437 - 540 °F | Average value: 255 °C Grade Count:14 |
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | Average value: 78.5 °C Grade Count:14 |
| Drying Temperature | 87.8 - 120 °C | 190 - 248 °F | Average value: 111 °C Grade Count:8 |
| Dry Time | 3.00 - 6.00 hour | 3.00 - 6.00 hour | Average value: 4.38 hour Grade Count:4 |
| Back Pressure | 0.000 - 1.38 MPa | 0.000 - 200 psi | Average value: 0.598 MPa Grade Count:3 |