- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 1.64
- 缺口冲击强度: 0.29
- 拉伸强度 [MPa]: 76.0
- 断裂伸长率 [%]: 68.0
- 弯曲强度 [MPa]: 20.5
- 弯曲模量 [MPa]: 4.61
- 热变形温度 [℃]: 216.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.64 - 1.84 g/cc | 0.0592 - 0.0665 lb/in³ | Average value: 1.71 g/cc Grade Count:30 |
| Filler Content | 45.0 - 50.0 % | 45.0 - 50.0 % | Average value: 47.9 % Grade Count:7 |
| Water Absorption | 0.000 - 0.400 % | 0.000 - 0.400 % | Average value: 0.182 % Grade Count:9 |
| Moisture Absorption at Equilibrium | 0.0300 - 0.500 % | 0.0300 - 0.500 % | Average value: 0.154 % Grade Count:10 |
| Water Absorption at Saturation | 0.400 - 0.500 % | 0.400 - 0.500 % | Average value: 0.425 % Grade Count:4 |
| Viscosity | 62000 - 766000 cP @Temperature 250 - 270 °C | 62000 - 766000 cP @Temperature 482 - 518 °F | Average value: 253000 cP Grade Count:1 |
| 62000 - 766000 cP @Shear Rate 100 - 10000 1/s | 62000 - 766000 cP @Shear Rate 100 - 10000 1/s | Average value: 253000 cP Grade Count:1 | |
| Viscosity Measurement | 70.0 - 120 @Temperature 240 - 300 °C | 70.0 - 120 @Temperature 464 - 572 °F | Average value: 99.5 Grade Count:1 |
| Linear Mold Shrinkage | 0.00100 - 0.00550 cm/cm | 0.00100 - 0.00550 in/in | Average value: 0.00276 cm/cm Grade Count:23 |
| Linear Mold Shrinkage, Transverse | 0.00400 - 0.0145 cm/cm | 0.00400 - 0.0145 in/in | Average value: 0.00931 cm/cm Grade Count:13 |
| Melt Flow | 2.00 - 30.0 g/10 min | 2.00 - 30.0 g/10 min | Average value: 10.4 g/10 min Grade Count:14 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 20.5 - 180 MPa | 2970 - 26100 psi | Average value: 123 MPa Grade Count:25 |
| 80.0 - 115 MPa @Temperature 60.0 - 120 °C | 11600 - 16700 psi @Temperature 140 - 248 °F | Average value: 61.1 MPa Grade Count:1 | |
| 12.68 - 119.6 MPa @Temperature 40.0 - 120 °C | 1839 - 17350 psi @Temperature 104 - 248 °F | Average value: 61.1 MPa Grade Count:2 | |
| 12.68 - 119.6 MPa @Strain 0.210 - 2.53 % | 1839 - 17350 psi @Strain 0.210 - 2.53 % | Average value: 61.1 MPa Grade Count:2 | |
| Tensile Strength, Yield | 76.0 - 150 MPa | 11000 - 21800 psi | Average value: 128 MPa Grade Count:5 |
| Elongation at Break | 1.00 - 3.00 % | 1.00 - 3.00 % | Average value: 2.00 % Grade Count:27 |
| Modulus of Elasticity | 4.10 - 18.7 GPa | 595 - 2710 ksi | Average value: 15.1 GPa Grade Count:24 |
| Flexural Yield Strength | 68.0 - 285 MPa | 9860 - 41300 psi | Average value: 212 MPa Grade Count:16 |
| Flexural Modulus | 4.61 - 16.5 GPa | 668 - 2400 ksi | Average value: 12.6 GPa Grade Count:20 |
| 7.50 - 10.0 GPa @Temperature 60.0 - 120 °C | 1090 - 1450 ksi @Temperature 140 - 248 °F | Average value: 8.67 GPa Grade Count:1 | |
| Shear Modulus | 0.409 - 2.78 GPa @Temperature -50.0 - 200 °C | 59.3 - 403 ksi @Temperature -58.0 - 392 °F | Average value: 1.43 GPa Grade Count:1 |
| Izod Impact, Notched | 0.290 - 2.67 J/cm | 0.543 - 5.00 ft-lb/in | Average value: 1.08 J/cm Grade Count:11 |
| 0.850 - 0.900 J/cm @Temperature -40.0 - -20.0 °C | 1.59 - 1.69 ft-lb/in @Temperature -40.0 - -4.00 °F | Average value: 0.875 J/cm Grade Count:1 | |
| Izod Impact, Unnotched | 7.47 - 10.1 J/cm | 14.0 - 19.0 ft-lb/in | Average value: 8.68 J/cm Grade Count:4 |
| Izod Impact, Notched (ISO) | 7.30 - 30.0 kJ/m² | 3.47 - 14.3 ft-lb/in² | Average value: 13.3 kJ/m² Grade Count:9 |
| 9.00 - 10.0 kJ/m² @Temperature -30.0 - -30.0 °C | 4.28 - 4.76 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 9.67 kJ/m² Grade Count:3 | |
| Izod Impact, Unnotched (ISO) | 33.0 - 80.0 kJ/m² | 15.7 - 38.1 ft-lb/in² | Average value: 52.0 kJ/m² Grade Count:3 |
| 43.0 - 50.0 kJ/m² @Temperature -30.0 - -30.0 °C | 20.5 - 23.8 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 46.5 kJ/m² Grade Count:2 | |
| Charpy Impact Unnotched | 2.20 - 7.00 J/cm² | 10.5 - 33.3 ft-lb/in² | Average value: 5.53 J/cm² Grade Count:16 |
| 4.00 - 6.90 J/cm² @Temperature -40.0 - 30.0 °C | 19.0 - 32.8 ft-lb/in² @Temperature -40.0 - 86.0 °F | Average value: 5.81 J/cm² Grade Count:13 | |
| Charpy Impact, Notched | 0.700 - 3.20 J/cm² | 3.33 - 15.2 ft-lb/in² | Average value: 1.25 J/cm² Grade Count:17 |
| 0.310 - 1.30 J/cm² @Temperature -30.0 - 30.0 °C | 1.48 - 6.19 ft-lb/in² @Temperature -22.0 - 86.0 °F | Average value: 1.08 J/cm² Grade Count:10 | |
| Tensile Creep Modulus, 1 hour | 0.000 - 15000 MPa | 0.000 - 2.18e+6 psi | Average value: 1740 MPa Grade Count:3 |
| 0.000 - 80.0 MPa @Temperature 60.0 - 60.0 °C | 0.000 - 11600 psi @Temperature 140 - 140 °F | Average value: 40.0 MPa Grade Count:1 | |
| 0.000 - 80.0 MPa @Strain 0.000 - 1.76 % | 0.000 - 11600 psi @Strain 0.000 - 1.76 % | Average value: 40.0 MPa Grade Count:1 | |
| Tensile Creep Modulus, 1000 hours | 0.000 - 11600 MPa | 0.000 - 1.68e+6 psi | Average value: 1290 MPa Grade Count:3 |
| 0.000 - 80.0 MPa @Temperature 60.0 - 60.0 °C | 0.000 - 11600 psi @Temperature 140 - 140 °F | Average value: 40.0 MPa Grade Count:1 | |
| 0.000 - 80.0 MPa @Strain 0.000 - 1.97 % | 0.000 - 11600 psi @Strain 0.000 - 1.97 % | Average value: 40.0 MPa Grade Count:1 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 7.00e+12 - 1.00e+17 ohm-cm | 7.00e+12 - 1.00e+17 ohm-cm | Average value: 1.02e+16 ohm-cm Grade Count:18 |
| Surface Resistance | 1.00e+13 - 4.00e+16 ohm | 1.00e+13 - 4.00e+16 ohm | Average value: 4.43e+15 ohm Grade Count:15 |
| Dielectric Constant | 3.20 - 4.90 | 3.20 - 4.90 | Average value: 4.17 Grade Count:10 |
| Dielectric Strength | 14.0 - 100 kV/mm | 356 - 2540 kV/in | Average value: 30.7 kV/mm Grade Count:16 |
| Dissipation Factor | 0.00120 - 0.0260 | 0.00120 - 0.0260 | Average value: 0.0116 Grade Count:8 |
| Comparative Tracking Index | 125 - 600 V | 125 - 600 V | Average value: 425 V Grade Count:13 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 2.00 - 500 µm/m-°C | 1.11 - 278 µin/in-°F | Average value: 198 µm/m-°C Grade Count:9 |
| CTE, linear, Transverse to Flow | 40.0 - 80.0 µm/m-°C | 22.2 - 44.4 µin/in-°F | Average value: 64.3 µm/m-°C Grade Count:5 |
| Melting Point | 200 - 250 °C | 392 - 482 °F | Average value: 223 °C Grade Count:16 |
| Maximum Service Temperature, Air | 75.0 - 435 °C | 167 - 815 °F | Average value: 183 °C Grade Count:5 |
| Deflection Temperature at 0.46 MPa (66 psi) | 216 - 228 °C | 420 - 442 °F | Average value: 222 °C Grade Count:21 |
| Deflection Temperature at 1.8 MPa (264 psi) | 193 - 220 °C | 379 - 428 °F | Average value: 210 °C Grade Count:29 |
| Vicat Softening Point | 210 - 225 °C | 410 - 437 °F | Average value: 216 °C Grade Count:8 |
| UL RTI, Electrical | 130 °C | 266 °F | Average value: 130 °C Grade Count:4 |
| UL RTI, Mechanical with Impact | 125 - 130 °C | 257 - 266 °F | Average value: 125 °C Grade Count:4 |
| UL RTI, Mechanical without Impact | 130 - 140 °C | 266 - 284 °F | Average value: 131 °C Grade Count:4 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:26 |
| Oxygen Index | 20.0 - 23.0 % | 20.0 - 23.0 % | Average value: 20.6 % Grade Count:5 |
| Glow Wire Test | 650 - 750 °C | 1200 - 1380 °F | Average value: 738 °C Grade Count:8 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 20.0 - 270 °C | 68.0 - 518 °F | Average value: 141 °C Grade Count:4 |
| Feed Temperature | 20.0 - 200 °C | 68.0 - 392 °F | Average value: 96.7 °C Grade Count:3 |
| Melt Temperature | 225 - 300 °C | 437 - 572 °F | Average value: 259 °C Grade Count:13 |
| Mold Temperature | 30.0 - 130 °C | 86.0 - 266 °F | Average value: 81.1 °C Grade Count:15 |
| Drying Temperature | 80.0 - 140 °C | 176 - 284 °F | Average value: 121 °C Grade Count:12 |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | Average value: 3.42 hour Grade Count:12 |
| Moisture Content | 0.0200 - 0.0800 % | 0.0200 - 0.0800 % | Average value: 0.0422 % Grade Count:9 |
| Dew Point | -30.0 - -28.9 °C | -22.0 - -20.0 °F | Average value: -29.4 °C Grade Count:4 |
| Injection Pressure | 60.0 - 103 MPa | 8700 - 15000 psi | Average value: 83.7 MPa Grade Count:5 |