- 密度 [g/cm3]: 1.6
- 缺口冲击强度: 0.587
- 弯曲模量 [MPa]: 6.21
- 热变形温度 [℃]: 216.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.60 g/cc | 0.0578 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 117 MPa @Thickness 3.17 mm | 17000 psi @Thickness 0.125 in | ASTM D638 |
| Elongation at Break | 3.0 % @Thickness 3.17 mm | 3.0 % @Thickness 0.125 in | ASTM D638 |
| Flexural Strength | 172 MPa @Thickness 3.17 mm | 25000 psi @Thickness 0.125 in | ASTM D790 |
| Flexural Modulus | 6.21 GPa @Thickness 3.17 mm | 900 ksi @Thickness 0.125 in | ASTM D790 |
| Izod Impact, Notched | 0.587 J/cm | 1.10 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 216 °C | 421 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 202 °C | 395 °F | ASTM D648 |
| UL RTI, Electrical | 75.0 °C | 167 °F | |
| UL RTI, Mechanical with Impact | 75.0 °C | 167 °F | |
| UL RTI, Mechanical without Impact | 75.0 °C | 167 °F | |
| Flammability, UL94 | V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | |
| 5VA @Thickness 2.50 mm | 5VA @Thickness 0.0984 in | ||