- 熔体流动速率 [g/10min]: 11.0
- 密度 [g/cm3]: 1.31
- 吸水率 [%]: 0.02
- 缺口冲击强度: 0.27
- 拉伸强度 [MPa]: 58.6
- 断裂伸长率 [%]: 74.5
- 弯曲强度 [MPa]: 46.9
- 弯曲模量 [MPa]: 2.76
- 硬度: 109.0
- 热变形温度 [℃]: 184.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.31 - 2.96 g/cc | 0.0473 - 0.107 lb/in³ | Average value: 1.64 g/cc Grade Count:45 |
| Filler Content | 10.0 - 30.0 % | 10.0 - 30.0 % | Average value: 21.0 % Grade Count:5 |
| Water Absorption | 0.0200 - 0.400 % | 0.0200 - 0.400 % | Average value: 0.0795 % Grade Count:20 |
| Moisture Absorption at Equilibrium | 0.0300 - 0.200 % | 0.0300 - 0.200 % | Average value: 0.153 % Grade Count:10 |
| Viscosity Test | 55.0 - 90.0 cm³/g | 55.0 - 90.0 cm³/g | Average value: 71.7 cm³/g Grade Count:3 |
| Linear Mold Shrinkage | 0.000 - 0.0160 cm/cm | 0.000 - 0.0160 in/in | Average value: 0.00462 cm/cm Grade Count:43 |
| Linear Mold Shrinkage, 6.35 mm section | 0.00400 - 0.0100 cm/cm | 0.00400 - 0.0100 in/in | Average value: 0.00700 cm/cm Grade Count:3 |
| Linear Mold Shrinkage, Transverse | 0.000 - 0.0130 cm/cm | 0.000 - 0.0130 in/in | Average value: 0.00688 cm/cm Grade Count:12 |
| Melt Flow | 11.0 - 30.0 g/10 min | 11.0 - 30.0 g/10 min | Average value: 20.2 g/10 min Grade Count:6 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 43.0 - 91.0 | 43.0 - 91.0 | Average value: 71.8 Grade Count:9 |
| Hardness, Rockwell R | 109 - 121 | 109 - 121 | Average value: 117 Grade Count:18 |
| Tensile Strength, Ultimate | 46.9 - 147 MPa | 6800 - 21300 psi | Average value: 96.5 MPa Grade Count:38 |
| Tensile Strength, Yield | 58.6 - 125 MPa | 8500 - 18100 psi | Average value: 91.7 MPa Grade Count:7 |
| Elongation at Break | 1.00 - 10.0 % | 1.00 - 10.0 % | Average value: 2.79 % Grade Count:39 |
| Elongation at Yield | 2.00 - 5.00 % | 2.00 - 5.00 % | Average value: 3.00 % Grade Count:3 |
| Modulus of Elasticity | 5.24 - 13.5 GPa | 760 - 1960 ksi | Average value: 9.38 GPa Grade Count:22 |
| Flexural Yield Strength | 74.5 - 220 MPa | 10800 - 31900 psi | Average value: 150 MPa Grade Count:42 |
| Flexural Modulus | 2.76 - 14.7 GPa | 400 - 2130 ksi | Average value: 8.68 GPa Grade Count:44 |
| Compressive Yield Strength | 53.8 - 124 MPa | 7800 - 18000 psi | Average value: 77.7 MPa Grade Count:3 |
| Izod Impact, Notched | 0.270 - 1.07 J/cm | 0.506 - 2.00 ft-lb/in | Average value: 0.620 J/cm Grade Count:36 |
| 0.85424 - 0.85424 J/cm @Temperature -30.0 - -30.0 °C | 1.6003 - 1.6003 ft-lb/in @Temperature -22.0 - -22.0 °F | Average value: 0.854 J/cm Grade Count:1 | |
| Izod Impact, Unnotched | 1.60 - 5.34 J/cm | 3.00 - 10.0 ft-lb/in | Average value: 4.21 J/cm Grade Count:15 |
| Izod Impact, Notched (ISO) | 3.10 - 14.0 kJ/m² | 1.48 - 6.66 ft-lb/in² | Average value: 6.06 kJ/m² Grade Count:18 |
| 4.00 - 8.00 kJ/m² @Temperature -30.0 - 30.0 °C | 1.90 - 3.81 ft-lb/in² @Temperature -22.0 - 86.0 °F | Average value: 5.63 kJ/m² Grade Count:4 | |
| Izod Impact, Unnotched (ISO) | 19.0 - 70.0 kJ/m² | 9.04 - 33.3 ft-lb/in² | Average value: 37.0 kJ/m² Grade Count:6 |
| 32.0 - 32.0 kJ/m² @Temperature -30.0 - -30.0 °C | 15.2 - 15.2 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 32.0 kJ/m² Grade Count:1 | |
| Charpy Impact Unnotched | 1.30 - 4.00 J/cm² | 6.19 - 19.0 ft-lb/in² | Average value: 2.89 J/cm² Grade Count:10 |
| 2.10 - 4.00 J/cm² @Temperature -30.0 - 30.0 °C | 9.99 - 19.0 ft-lb/in² @Temperature -22.0 - 86.0 °F | Average value: 2.89 J/cm² Grade Count:8 | |
| Charpy Impact, Notched | 0.400 - 1.21 J/cm² | 1.90 - 5.76 ft-lb/in² | Average value: 0.629 J/cm² Grade Count:16 |
| 0.300 - 0.720 J/cm² @Temperature -30.0 - 30.0 °C | 1.43 - 3.43 ft-lb/in² @Temperature -22.0 - 86.0 °F | Average value: 0.572 J/cm² Grade Count:9 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+14 - 1.00e+17 ohm-cm | 1.00e+14 - 1.00e+17 ohm-cm | Average value: 1.54e+16 ohm-cm Grade Count:27 |
| Surface Resistance | 1.00e+13 - 1.00e+17 ohm | 1.00e+13 - 1.00e+17 ohm | Average value: 2.61e+16 ohm Grade Count:10 |
| Dielectric Constant | 3.00 - 5.10 | 3.00 - 5.10 | Average value: 3.80 Grade Count:17 |
| Dielectric Strength | 17.0 - 100 kV/mm | 432 - 2540 kV/in | Average value: 24.8 kV/mm Grade Count:25 |
| Dissipation Factor | 0.00100 - 0.0400 | 0.00100 - 0.0400 | Average value: 0.0152 Grade Count:16 |
| Arc Resistance | 60.0 - 130 sec | 60.0 - 130 sec | Average value: 118 sec Grade Count:11 |
| Comparative Tracking Index | 125 - 600 V | 125 - 600 V | Average value: 307 V Grade Count:11 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 4.00 - 55.8 µm/m-°C | 2.22 - 31.0 µin/in-°F | Average value: 25.5 µm/m-°C Grade Count:19 |
| 25.2 - 25.2 µm/m-°C @Temperature 60.0 - 138 °C | 14.0 - 14.0 µin/in-°F @Temperature 140 - 280 °F | Average value: 25.2 µm/m-°C Grade Count:2 | |
| CTE, linear, Transverse to Flow | 46.0 - 97.0 µm/m-°C | 25.6 - 53.9 µin/in-°F | Average value: 74.6 µm/m-°C Grade Count:10 |
| Melting Point | 210 - 268 °C | 410 - 514 °F | Average value: 225 °C Grade Count:20 |
| Deflection Temperature at 0.46 MPa (66 psi) | 184 - 223 °C | 363 - 433 °F | Average value: 214 °C Grade Count:35 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.6 - 220 °C | 150 - 428 °F | Average value: 190 °C Grade Count:44 |
| Vicat Softening Point | 150 - 220 °C | 302 - 428 °F | Average value: 193 °C Grade Count:6 |
| Glass Transition Temp, Tg | 54.0 - 60.0 °C | 129 - 140 °F | Average value: 56.0 °C Grade Count:3 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:30 |
| Glow Wire Test | 750 - 960 °C | 1380 - 1760 °F | Average value: 908 °C Grade Count:3 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 20.0 - 280 °C | 68.0 - 536 °F | Average value: 136 °C Grade Count:22 |
| Feed Temperature | 230 - 250 °C | 446 - 482 °F | Average value: 239 °C Grade Count:9 |
| Nozzle Temperature | 250 - 280 °C | 482 - 536 °F | Average value: 263 °C Grade Count:4 |
| Die Temperature | 240 - 265 °C | 464 - 509 °F | Average value: 252 °C Grade Count:9 |
| Melt Temperature | 225 - 280 °C | 437 - 536 °F | Average value: 248 °C Grade Count:13 |
| Mold Temperature | 40.0 - 120 °C | 104 - 248 °F | Average value: 82.9 °C Grade Count:19 |
| Injection Velocity | 300 mm/sec | 11.8 in/sec | Average value: 300 mm/sec Grade Count:9 |
| Drying Temperature | 120 - 130 °C | 248 - 266 °F | Average value: 125 °C Grade Count:11 |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Average value: 3.91 hour Grade Count:11 |
| Moisture Content | 0.0200 - 0.0300 % | 0.0200 - 0.0300 % | Average value: 0.0210 % Grade Count:10 |
| Injection Pressure | 48.0 - 140 MPa | 6960 - 20300 psi | Average value: 76.2 MPa Grade Count:12 |
| Hold Pressure | 30.0 - 80.0 MPa | 4350 - 11600 psi | Average value: 49.4 MPa Grade Count:5 |
| Back Pressure | 0.000 - 20.0 MPa | 0.000 - 2900 psi | Average value: 3.87 MPa Grade Count:4 |
| Hot-Working Temperature | 250 - 265 °C | 482 - 509 °F | Average value: 257 °C Grade Count:9 |