- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 1.17
- 吸水率 [%]: 0.03
- 缺口冲击强度: 8.01
- 拉伸强度 [MPa]: 51.0
- 断裂伸长率 [%]: 85.5
- 弯曲模量 [MPa]: 1.86
- 热变形温度 [℃]: 116.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in³ | ASTM D792 |
| Water Absorption | 0.030 % | 0.030 % | 24 hours at 73°C; ASTM D570 |
| Linear Mold Shrinkage | 0.0075 cm/cm | 0.0075 in/in | ASTM D955 |
| Melt Flow | 2.0 g/10 min @Load 5.00 kg, Temperature 250 °C | 2.0 g/10 min @Load 11.0 lb, Temperature 482 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 51.0 MPa @Thickness 3.17 mm | 7400 psi @Thickness 0.125 in | ASTM D638 |
| Elongation at Break | 150 % @Thickness 3.17 mm | 150 % @Thickness 0.125 in | ASTM D638 |
| Flexural Yield Strength | 85.5 MPa @Thickness 3.17 mm | 12400 psi @Thickness 0.125 in | ASTM D790 |
| Flexural Modulus | 1.86 GPa @Thickness 3.17 mm | 270 ksi @Thickness 0.125 in | ASTM D790 |
| Izod Impact, Notched | 8.01 J/cm @Thickness 3.17 mm | 15.0 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 116 °C | 241 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C | 205 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 232 - 243 °C | 450 - 470 °F | |
| Middle Barrel Temperature | 238 - 254 °C | 460 - 490 °F | |
| Front Barrel Temperature | 246 - 268 °C | 475 - 515 °F | |
| Nozzle Temperature | 246 - 266 °C | 475 - 510 °F | |
| Melt Temperature | 243 - 279 °C | 470 - 535 °F | |
| Mold Temperature | 65.6 - 82.2 °C | 150 - 180 °F | |
| Drying Temperature | 110 °C | 230 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Back Pressure | 0.000 - 3.45 MPa | 0.000 - 500 psi | |
| Shot Size | 50 - 80 % | 50 - 80 % | |
| Screw Speed | 20 - 60 rpm | 20 - 60 rpm | |