- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 1.14
- 吸水率 [%]: 0.02
- 缺口冲击强度: 0.15
- 拉伸强度 [MPa]: 55.0
- 断裂伸长率 [%]: 80.0
- 弯曲强度 [MPa]: 8.17
- 弯曲模量 [MPa]: 0.00800
- 硬度: 90.0
- 热变形温度 [℃]: 160.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 - 1.97 g/cc | 0.0412 - 0.0712 lb/in³ | Average value: 1.56 g/cc Grade Count:308 |
| Filler Content | 25.0 - 30.0 % | 25.0 - 30.0 % | Average value: 29.8 % Grade Count:64 |
| Water Absorption | 0.0200 - 1.00 % | 0.0200 - 1.00 % | Average value: 0.223 % Grade Count:96 |
| Moisture Absorption at Equilibrium | 0.0300 - 0.200 % | 0.0300 - 0.200 % | Average value: 0.132 % Grade Count:108 |
| Water Absorption at Saturation | 0.250 - 5.20 % | 0.250 - 5.20 % | Average value: 0.653 % Grade Count:19 |
| Viscosity | 35000 - 998000 cP @Temperature 240 - 270 °C | 35000 - 998000 cP @Temperature 464 - 518 °F | Average value: 266000 cP Grade Count:5 |
| 35000 - 998000 cP @Shear Rate 100 - 10000 1/s | 35000 - 998000 cP @Shear Rate 100 - 10000 1/s | Average value: 266000 cP Grade Count:5 | |
| Viscosity Measurement | 95.0 - 108 | 95.0 - 108 | Average value: 104 Grade Count:7 |
| Viscosity Test | 62.0 - 111 cm³/g | 62.0 - 111 cm³/g | Average value: 88.5 cm³/g Grade Count:28 |
| Maximum Moisture Content | 0.0200 | 0.0200 | Average value: 0.0200 Grade Count:12 |
| Linear Mold Shrinkage | 0.000 - 0.0200 cm/cm | 0.000 - 0.0200 in/in | Average value: 0.00472 cm/cm Grade Count:252 |
| Linear Mold Shrinkage, 6.35 mm section | 0.00400 cm/cm | 0.00400 in/in | Average value: 0.00400 cm/cm Grade Count:5 |
| Linear Mold Shrinkage, Transverse | 0.00100 - 0.0210 cm/cm | 0.00100 - 0.0210 in/in | Average value: 0.00947 cm/cm Grade Count:114 |
| Melt Flow | 1.00 - 63.0 g/10 min | 1.00 - 63.0 g/10 min | Average value: 19.6 g/10 min Grade Count:106 |
| Ash | 28.0 - 34.0 % | 28.0 - 34.0 % | Average value: 30.4 % Grade Count:5 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 71.0 - 112 | 71.0 - 112 | Average value: 89.5 Grade Count:34 |
| Hardness, Rockwell R | 90.0 - 122 | 90.0 - 122 | Average value: 116 Grade Count:30 |
| Hardness, Shore D | 79.0 - 89.0 | 79.0 - 89.0 | Average value: 82.9 Grade Count:8 |
| Ball Indentation Hardness | 105 - 250 MPa | 15200 - 36300 psi | Average value: 190 MPa Grade Count:12 |
| Tensile Strength, Ultimate | 8.17 - 190 MPa | 1180 - 27600 psi | Average value: 113 MPa Grade Count:245 |
| 23.0 - 222 MPa @Temperature -40.0 - 150 °C | 3340 - 32200 psi @Temperature -40.0 - 302 °F | Average value: 64.4 MPa Grade Count:10 | |
| 3.26 - 200 MPa @Temperature -40.0 - 160 °C | 473 - 29000 psi @Temperature -40.0 - 320 °F | Average value: 64.4 MPa Grade Count:8 | |
| 3.26 - 200 MPa @Strain 0.100 - 7.73 % | 473 - 29000 psi @Strain 0.100 - 7.73 % | Average value: 64.4 MPa Grade Count:8 | |
| Tensile Strength, Yield | 55.0 - 155 MPa | 7980 - 22500 psi | Average value: 119 MPa Grade Count:73 |
| Elongation at Break | 1.00 - 130 % | 1.00 - 130 % | Average value: 3.63 % Grade Count:259 |
| 1.90 - 5.70 % @Temperature -40.0 - 150 °C | 1.90 - 5.70 % @Temperature -40.0 - 302 °F | Average value: 3.40 % Grade Count:6 | |
| Elongation at Yield | 2.00 - 5.00 % | 2.00 - 5.00 % | Average value: 2.97 % Grade Count:9 |
| Modulus of Elasticity | 0.824 - 11.8 GPa | 119 - 1710 ksi | Average value: 9.41 GPa Grade Count:167 |
| 1.527 - 11.243 GPa @Temperature -40.0 - 176 °C | 221.5 - 1630.7 ksi @Temperature -40.0 - 349 °F | Average value: 6.81 GPa Grade Count:7 | |
| Flexural Yield Strength | 80.0 - 270 MPa | 11600 - 39200 psi | Average value: 185 MPa Grade Count:229 |
| 75.0 - 286 MPa @Temperature -40.0 - 150 °C | 10900 - 41500 psi @Temperature -40.0 - 302 °F | Average value: 144 MPa Grade Count:3 | |
| Flexural Modulus | 0.00800 - 11.0 GPa | 1.16 - 1600 ksi | Average value: 8.29 GPa Grade Count:230 |
| 1.30 - 9.60 GPa @Temperature -40.0 - 150 °C | 189 - 1390 ksi @Temperature -40.0 - 302 °F | Average value: 5.15 GPa Grade Count:6 | |
| Compressive Yield Strength | 117 - 202 MPa | 17000 - 29300 psi | Average value: 133 MPa Grade Count:7 |
| Shear Modulus | 0.380 - 2.43 GPa @Temperature -50.0 - 200 °C | 55.1 - 352 ksi @Temperature -58.0 - 392 °F | Average value: 1.28 GPa Grade Count:2 |
| Izod Impact, Notched | 0.150 - 2.19 J/cm | 0.281 - 4.10 ft-lb/in | Average value: 0.899 J/cm Grade Count:144 |
| 0.800 - 1.01 J/cm @Temperature -40.0 - -20.0 °C | 1.50 - 1.89 ft-lb/in @Temperature -40.0 - -4.00 °F | Average value: 0.890 J/cm Grade Count:5 | |
| Izod Impact, Unnotched | 1.08 - 9.98 J/cm | 2.02 - 18.7 ft-lb/in | Average value: 7.19 J/cm Grade Count:26 |
| 7.36 - 11.2 J/cm @Temperature -40.0 - -40.0 °C | 13.8 - 21.0 ft-lb/in @Temperature -40.0 - -40.0 °F | Average value: 9.28 J/cm Grade Count:2 | |
| Izod Impact, Notched (ISO) | 4.50 - 70.0 kJ/m² | 2.14 - 33.3 ft-lb/in² | Average value: 11.4 kJ/m² Grade Count:92 |
| 6.00 - 12.0 kJ/m² @Temperature -40.0 - 30.0 °C | 2.86 - 5.71 ft-lb/in² @Temperature -40.0 - 86.0 °F | Average value: 8.51 kJ/m² Grade Count:25 | |
| Izod Impact, Unnotched (ISO) | 35.0 - 70.0 kJ/m² | 16.7 - 33.3 ft-lb/in² | Average value: 52.2 kJ/m² Grade Count:46 |
| 30.0 - 60.0 kJ/m² @Temperature -40.0 - -30.0 °C | 14.3 - 28.6 ft-lb/in² @Temperature -40.0 - -22.0 °F | Average value: 45.9 kJ/m² Grade Count:16 | |
| Charpy Impact Unnotched | 1.50 - 50.0 J/cm² | 7.14 - 238 ft-lb/in² | Average value: 5.72 J/cm² Grade Count:119 |
| 1.40 - 8.00 J/cm² @Temperature -40.0 - 30.0 °C | 6.66 - 38.1 ft-lb/in² @Temperature -40.0 - 86.0 °F | Average value: 5.15 J/cm² Grade Count:80 | |
| Charpy Impact, Notched | 0.210 - 7.50 J/cm² | 0.999 - 35.7 ft-lb/in² | Average value: 0.993 J/cm² Grade Count:141 |
| 0.300 - 1.60 J/cm² @Temperature -40.0 - 30.0 °C | 1.43 - 7.61 ft-lb/in² @Temperature -40.0 - 86.0 °F | Average value: 0.905 J/cm² Grade Count:81 | |
| Dart Drop, Total Energy | 5.00 J | 3.69 ft-lb | Average value: 5.00 J Grade Count:3 |
| Puncture Energy | 1.90 - 2.30 J | 1.40 - 1.70 ft-lb | Average value: 2.22 J Grade Count:5 |
| 1.70 - 2.50 J @Temperature -30.0 - -30.0 °C | 1.25 - 1.84 ft-lb @Temperature -22.0 - -22.0 °F | Average value: 2.10 J Grade Count:3 | |
| Tensile Creep Modulus, 1 hour | 0.000 - 11000 MPa | 0.000 - 1.60e+6 psi | Average value: 3470 MPa Grade Count:11 |
| 0.000 - 60.0 MPa @Temperature 60.0 - 60.0 °C | 0.000 - 8700 psi @Temperature 140 - 140 °F | Average value: 30.0 MPa Grade Count:1 | |
| 0.000 - 60.0 MPa @Strain 0.000 - 1.29 % | 0.000 - 8700 psi @Strain 0.000 - 1.29 % | Average value: 30.0 MPa Grade Count:1 | |
| Tensile Creep Modulus, 1000 hours | 0.000 - 10000 MPa | 0.000 - 1.45e+6 psi | Average value: 1600 MPa Grade Count:16 |
| 0.000 - 60.0 MPa @Temperature 60.0 - 60.0 °C | 0.000 - 8700 psi @Temperature 140 - 140 °F | Average value: 30.0 MPa Grade Count:1 | |
| 0.000 - 60.0 MPa @Strain 0.000 - 1.36 % | 0.000 - 8700 psi @Strain 0.000 - 1.36 % | Average value: 30.0 MPa Grade Count:1 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+8 - 1.20e+17 ohm-cm | 1.00e+8 - 1.20e+17 ohm-cm | Average value: 1.64e+16 ohm-cm Grade Count:164 |
| Surface Resistance | 1.00e+8 - 2.00e+17 ohm | 1.00e+8 - 2.00e+17 ohm | Average value: 1.58e+16 ohm Grade Count:108 |
| Dielectric Constant | 2.50 - 5.10 | 2.50 - 5.10 | Average value: 3.78 Grade Count:123 |
| Dielectric Strength | 14.8 - 100 kV/mm | 375 - 2540 kV/in | Average value: 25.8 kV/mm Grade Count:151 |
| Dissipation Factor | 0.00100 - 0.0520 | 0.00100 - 0.0520 | Average value: 0.0106 Grade Count:90 |
| Dielectric Loss Index | 0.00200 - 0.0200 | 0.00200 - 0.0200 | Average value: 0.0187 Grade Count:14 |
| Arc Resistance | 60.0 - 180 sec | 60.0 - 180 sec | Average value: 109 sec Grade Count:38 |
| Comparative Tracking Index | 50.0 - 600 V | 50.0 - 600 V | Average value: 351 V Grade Count:121 |
| Hot Wire Ignition, HWI | 7.00 - 120 sec | 7.00 - 120 sec | Average value: 40.6 sec Grade Count:11 |
| High Amp Arc Ignition, HAI | 30.0 - 120 arcs | 30.0 - 120 arcs | Average value: 96.4 arcs Grade Count:11 |
| High Voltage Arc-Tracking Rate, HVTR | 25.4 - 150 mm/min | 1.00 - 5.91 in/min | Average value: 110 mm/min Grade Count:8 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 0.200 - 500 µm/m-°C | 0.111 - 278 µin/in-°F | Average value: 69.4 µm/m-°C Grade Count:112 |
| CTE, linear, Transverse to Flow | 24.0 - 140 µm/m-°C | 13.3 - 77.8 µin/in-°F | Average value: 91.1 µm/m-°C Grade Count:66 |
| Specific Heat Capacity | 1.40 - 1.73 J/g-°C | 0.335 - 0.413 BTU/lb-°F | Average value: 1.57 J/g-°C Grade Count:5 |
| Thermal Conductivity | 0.166 - 0.320 W/m-K | 1.15 - 2.22 BTU-in/hr-ft²-°F | Average value: 0.233 W/m-K Grade Count:12 |
| Melting Point | 200 - 255 °C | 392 - 491 °F | Average value: 224 °C Grade Count:129 |
| Maximum Service Temperature, Air | 75.0 - 350 °C | 167 - 662 °F | Average value: 177 °C Grade Count:21 |
| Transformation Temperature, Tg | 41.0 - 60.0 °C | 106 - 140 °F | Average value: 56.7 °C Grade Count:13 |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 - 230 °C | 320 - 446 °F | Average value: 217 °C Grade Count:229 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 - 230 °C | 158 - 446 °F | Average value: 201 °C Grade Count:282 |
| Deflection Temperature at 5.0 MPa | 130 - 186 °C | 266 - 367 °F | Average value: 165 °C Grade Count:3 |
| Deflection Temperature at 8.0 MPa | 70.0 - 165 °C | 158 - 329 °F | Average value: 138 °C Grade Count:24 |
| Vicat Softening Point | 150 - 230 °C | 302 - 446 °F | Average value: 210 °C Grade Count:73 |
| Glass Transition Temp, Tg | 19.0 - 120 °C | 66.2 - 248 °F | Average value: 63.5 °C Grade Count:4 |
| Decomposition Temperature | 290 - 300 °C | 554 - 572 °F | Average value: 292 °C Grade Count:5 |
| UL RTI, Electrical | 60.0 - 140 °C | 140 - 284 °F | Average value: 130 °C Grade Count:25 |
| UL RTI, Mechanical with Impact | 60.0 - 150 °C | 140 - 302 °F | Average value: 125 °C Grade Count:25 |
| UL RTI, Mechanical without Impact | 60.0 - 140 °C | 140 - 284 °F | Average value: 130 °C Grade Count:25 |
| Flammability, UL94 | HB - 5VA | HB - 5VA | Grade Count:277 |
| Flammability Test | 15.0 - 30.0 | 15.0 - 30.0 | Average value: 20.7 Grade Count:3 |
| Oxygen Index | 19.0 - 43.7 % | 19.0 - 43.7 % | Average value: 25.4 % Grade Count:40 |
| Glow Wire Test | 650 - 960 °C | 1200 - 1760 °F | Average value: 829 °C Grade Count:57 |
| Shrinkage | 0.0700 - 0.260 % | 0.0700 - 0.260 % | Average value: 0.116 % Grade Count:4 |
| 0.100 - 0.100 % @Temperature 120 - 120 °C | 0.100 - 0.100 % @Temperature 248 - 248 °F | Average value: 0.100 % Grade Count:1 | |
| 0.100 - 0.100 % @Time 14400 - 14400 sec | 0.100 - 0.100 % @Time 4.00 - 4.00 hour | Average value: 0.100 % Grade Count:1 | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 20.0 - 280 °C | 68.0 - 536 °F | Average value: 116 °C Grade Count:57 |
| Feed Temperature | 20.0 - 260 °C | 68.0 - 500 °F | Average value: 193 °C Grade Count:40 |
| Nozzle Temperature | 225 - 271 °C | 437 - 520 °F | Average value: 252 °C Grade Count:63 |
| Die Temperature | 240 - 275 °C | 464 - 527 °F | Average value: 256 °C Grade Count:30 |
| Melt Temperature | 206 - 300 °C | 403 - 572 °F | Average value: 247 °C Grade Count:157 |
| Mold Temperature | 30.0 - 130 °C | 86.0 - 266 °F | Average value: 80.0 °C Grade Count:171 |
| Injection Velocity | 200 - 300 mm/sec | 7.87 - 11.8 in/sec | Average value: 286 mm/sec Grade Count:21 |
| Drying Temperature | 80.0 - 140 °C | 176 - 284 °F | Average value: 122 °C Grade Count:116 |
| Dry Time | 2.00 - 12.0 hour | 2.00 - 12.0 hour | Average value: 3.91 hour Grade Count:117 |
| 2.00 - 8.00 hour @Temperature 113 - 120 °C | 2.00 - 8.00 hour @Temperature 235 - 248 °F | Average value: 5.40 hour Grade Count:5 | |
| Moisture Content | 0.000 - 0.200 % | 0.000 - 0.200 % | Average value: 0.0378 % Grade Count:77 |
| Dew Point | -30.0 - -28.9 °C | -22.0 - -20.0 °F | Average value: -29.2 °C Grade Count:16 |
| Injection Pressure | 4.96 - 124 MPa | 720 - 18000 psi | Average value: 76.7 MPa Grade Count:57 |
| Hold Pressure | 30.0 - 100 MPa | 4350 - 14500 psi | Average value: 57.7 MPa Grade Count:33 |
| Back Pressure | 0.000 - 18.0 MPa | 0.000 - 2610 psi | Average value: 2.92 MPa Grade Count:51 |
| Shot Size | 30.0 - 80.0 % | 30.0 - 80.0 % | Average value: 57.1 % Grade Count:7 |
| Vent Depth | 0.00127 - 0.00381 cm | 0.000500 - 0.00150 in | Average value: 0.00275 cm Grade Count:3 |
| Screw Speed | 20.0 - 120 rpm | 20.0 - 120 rpm | Average value: 81.3 rpm Grade Count:33 |
| Hot-Working Temperature | 250 - 275 °C | 482 - 527 °F | Average value: 256 °C Grade Count:30 |