- 熔体流动速率 [g/10min]: 16.5
- 密度 [g/cm3]: 1.33
- 吸水率 [%]: 0.05
- 缺口冲击强度: 0.32
- 拉伸强度 [MPa]: 43.0
- 断裂伸长率 [%]: 50.0
- 弯曲强度 [MPa]: 33.0
- 弯曲模量 [MPa]: 1.70
- 热变形温度 [℃]: 143.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 - 1.65 g/cc | 0.0480 - 0.0596 lb/in³ | Average value: 1.42 g/cc Grade Count:31 |
| Filler Content | 10.0 - 20.0 % | 10.0 - 20.0 % | Average value: 14.1 % Grade Count:8 |
| Water Absorption | 0.0500 - 0.150 % | 0.0500 - 0.150 % | Average value: 0.0850 % Grade Count:16 |
| Additive Loading | 5.00 - 10.0 % | 5.00 - 10.0 % | Average value: 6.67 % Grade Count:3 |
| Linear Mold Shrinkage | 0.000700 - 0.0250 cm/cm | 0.000700 - 0.0250 in/in | Average value: 0.0182 cm/cm Grade Count:29 |
| Melt Flow | 16.5 - 23.8 g/10 min | 16.5 - 23.8 g/10 min | Average value: 20.5 g/10 min Grade Count:5 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 33.0 - 100 MPa | 4790 - 14500 psi | Average value: 47.7 MPa Grade Count:29 |
| Tensile Strength, Yield | 43.0 - 53.1 MPa | 6240 - 7700 psi | Average value: 47.9 MPa Grade Count:3 |
| Elongation at Break | 3.00 - 12.0 % | 3.00 - 12.0 % | Average value: 8.89 % Grade Count:18 |
| Elongation at Yield | 2.80 - 12.0 % | 2.80 - 12.0 % | Average value: 5.19 % Grade Count:9 |
| Modulus of Elasticity | 2.00 - 6.00 GPa | 290 - 870 ksi | Average value: 2.69 GPa Grade Count:25 |
| Flexural Yield Strength | 50.0 - 100 MPa | 7250 - 14500 psi | Average value: 73.8 MPa Grade Count:25 |
| Flexural Modulus | 1.70 - 4.00 GPa | 247 - 580 ksi | Average value: 2.37 GPa Grade Count:29 |
| Izod Impact, Notched | 0.320 - 0.694 J/cm | 0.600 - 1.30 ft-lb/in | Average value: 0.489 J/cm Grade Count:19 |
| Izod Impact, Unnotched | 3.47 - 8.54 J/cm | 6.50 - 16.0 ft-lb/in | Average value: 5.84 J/cm Grade Count:14 |
| Izod Impact, Notched (ISO) | 3.00 - 7.00 kJ/m² | 1.43 - 3.33 ft-lb/in² | Average value: 4.65 kJ/m² Grade Count:4 |
| 6.00 - 6.00 kJ/m² @Temperature -30.0 - -30.0 °C | 2.86 - 2.86 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 6.00 kJ/m² Grade Count:1 | |
| Charpy Impact Unnotched | 1.90 - 10.0 J/cm² | 9.04 - 47.6 ft-lb/in² | Average value: 3.38 J/cm² Grade Count:9 |
| Coefficient of Friction | 0.150 - 0.390 | 0.150 - 0.390 | Average value: 0.197 Grade Count:7 |
| Coefficient of Friction, Static | 0.0800 - 0.210 | 0.0800 - 0.210 | Average value: 0.126 Grade Count:7 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+14 - 3.00e+16 ohm-cm | 1.00e+14 - 3.00e+16 ohm-cm | Average value: 1.00e+16 ohm-cm Grade Count:10 |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | Average value: 1.00e+14 ohm Grade Count:3 |
| Insulation Resistance | 1.00e+12 ohm | 1.00e+12 ohm | Average value: 1.00e+12 ohm Grade Count:8 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 32.4 - 109 µm/m-°C | 18.0 - 60.6 µin/in-°F | Average value: 76.5 µm/m-°C Grade Count:3 |
| Maximum Service Temperature, Air | 130 - 150 °C | 266 - 302 °F | Average value: 140 °C Grade Count:8 |
| Deflection Temperature at 0.46 MPa (66 psi) | 143 - 215 °C | 290 - 419 °F | Average value: 171 °C Grade Count:4 |
| Deflection Temperature at 1.8 MPa (264 psi) | 54.4 - 190 °C | 130 - 374 °F | Average value: 68.5 °C Grade Count:21 |
| Vicat Softening Point | 165 - 210 °C | 329 - 410 °F | Average value: 187 °C Grade Count:5 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:18 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 232 - 270 °C | 450 - 518 °F | Average value: 250 °C Grade Count:11 |
| Nozzle Temperature | 250 - 265 °C | 482 - 509 °F | Average value: 258 °C Grade Count:8 |
| Melt Temperature | 230 - 280 °C | 446 - 536 °F | Average value: 257 °C Grade Count:26 |
| Mold Temperature | 49.0 - 120 °C | 120 - 248 °F | Average value: 88.3 °C Grade Count:29 |
| Drying Temperature | 80.0 - 130 °C | 176 - 266 °F | Average value: 109 °C Grade Count:27 |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | Average value: 3.77 hour Grade Count:13 |
| 2.00 - 4.00 hour @Temperature 121 - 121 °C | 2.00 - 4.00 hour @Temperature 250 - 250 °F | Average value: 3.00 hour Grade Count:1 | |
| Moisture Content | 0.0300 - 0.150 % | 0.0300 - 0.150 % | Average value: 0.0447 % Grade Count:15 |
| Dew Point | -28.9 °C | -20.0 °F | Average value: -28.9 °C Grade Count:12 |
| Injection Pressure | 4.96 - 103 MPa | 720 - 15000 psi | Average value: 75.9 MPa Grade Count:14 |