- 熔体流动速率 [g/10min]: 33.7
- 密度 [g/cm3]: 1.53
- 吸水率 [%]: 0.4
- 拉伸强度 [MPa]: 135.0
- 热变形温度 [℃]: 221.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.53 g/cc | 0.0553 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.40 % | 0.40 % | DIN 53495/1L | ||
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C/50% R.H. | ||
| Viscosity Test | 87 cm³/g | 87 cm³/g | Viscosity number; ISO 1628 | ||
| Linear Mold Shrinkage, Flow | 0.0036 cm/cm | 0.0036 in/in | 60x60x2mm; ISO 294 | ||
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm | 0.011 in/in | 60x60x2mm; ISO 294 | ||
| Melt Flow | 33.7 g/10 min @Load 2.16 kg, Temperature 250 °C | 33.7 g/10 min @Load 4.76 lb, Temperature 482 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 135 MPa | 19600 psi | 50mm/min; ISO 527-2 | ||
| Elongation at Break | 2.6 % | 2.6 % | 50mm/min; ISO 527 | ||
| Modulus of Elasticity | 9.70 GPa | 1410 ksi | ISO 527-2 | ||
| Charpy Impact Unnotched | 50.0 J/cm² | 238 ft-lb/in² | ISO 179/1eU | ||
| Charpy Impact, Notched | 7.50 J/cm² | 35.7 ft-lb/in² | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Comparative Tracking Index | 350 V | 350 V | Test Solution A; IEC 112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 - 225 °C | 428 - 437 °F | |||
| Maximum Service Temperature, Air | 210 °C | 410 °F | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 221 °C | 430 °F | ISO 75-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 202 °C | 396 °F | ISO 75-2 | ||
| Flammability, UL94 | HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | |||
| HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 250 - 275 °C | 482 - 527 °F | Injection molding | ||
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | |||
| Descriptive Properties | |||||
| Color | Natural and Black | ||||
| Commercial Status | North America and Europe | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||