- 熔体流动速率 [g/10min]: 22.0
- 密度 [g/cm3]: 1.42
- 吸水率 [%]: 0.4
- 缺口冲击强度: 0.43
- 弯曲强度 [MPa]: 93.0
- 弯曲模量 [MPa]: 4.80
- 热变形温度 [℃]: 220.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.40 % | 0.40 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C/50% R.H.; ISO 62 | ||
| Viscosity Test | 111 cm³/g | 111 cm³/g | Viscosity number | ||
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | ASTM Data; MD | ||
| Melt Flow | 22 g/10 min @Load 2.16 kg, Temperature 250 °C | 22 g/10 min @Load 4.76 lb, Temperature 482 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 93.0 MPa | 13500 psi | 0.2 in/min; ASTM Test | ||
| Tensile Strength, Ultimate | 93.0 MPa | 13500 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 4.0 % | 4.0 % | 5mm/min; ISO 527 | ||
| 4.0 % | 4.0 % | 0.2 in/min; ASTM Test | |||
| Tensile Modulus | 5.52 GPa | 801 ksi | ASTM Test | ||
| 6.00 GPa | 870 ksi | 1mm/min; ISO 527 | |||
| Flexural Modulus | 4.80 GPa | 696 ksi | ISO Data | ||
| 4.83 GPa | 701 ksi | ASTM Test | |||
| Izod Impact, Notched | 0.430 J/cm @Temperature -40.0 °C | 0.806 ft-lb/in @Temperature -40.0 °F | ASTM Test | ||
| 0.530 J/cm @Thickness 3.17 mm | 0.993 ft-lb/in @Thickness 0.125 in | ASTM Test | |||
| Izod Impact, Notched (ISO) | 8.50 kJ/m² | 4.04 ft-lb/in² | ISO Test | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 | ||
| Dielectric Constant | 3.7 @Frequency 100 Hz | 3.7 @Frequency 100 Hz | IEC 60250 | ||
| 3.7 @Frequency 1.00e+6 Hz | 3.7 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Dissipation Factor | 0.0012 @Frequency 100 Hz | 0.0012 @Frequency 100 Hz | IEC 60250 | ||
| 0.015 @Frequency 1.00e+6 Hz | 0.015 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 40.0 µm/m-°C | 22.2 µin/in-°F | ISO 11359 | ||
| Melting Point | 223 °C | 433 °F | 10 K/min | ||
| 223 °C | 433 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ASTM Test | ||
| 220 °C | 428 °F | ISO 75 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 183 °C | 361 °F | ISO 75 | ||
| 203 °C | 397 °F | ASTM Test | |||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |||
| HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 265 °C | 509 °F | Injection molding | ||
| Injection Velocity | 70.0 mm/sec | 2.76 in/sec | Injection molding | ||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| NSF Std. 61 | Yes | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| Special characteristic | Heat stabilized or stable to heat | ||||
| Light stabilized or stable to light | |||||
| Lubricant | |||||
| U.V. stabilized or stable to weather | |||||