DuPont Performance Polymers Crastin® SK642FR NC010 PBT

DuPont Performance Polymers Crastin® SK642FR NC010 PBT 物性表: DuPont Performance Polymers Crastin® SK642FR NC010 PBT物性表及特性介绍,DuPont Performance Polymers Crastin® SK642FR NC010 PBT注塑参数详情,如需DuPont Performance Polymers Crastin® SK642FR NC010 PBT下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.58
  • 吸水率 [%]: 0.14
  • 缺口冲击强度: 6.0
  • 热变形温度 [℃]: 218.0
 
Physical PropertiesMetricEnglishComments
Density 1.58 g/cc0.0571 lb/in³ISO 1183
Filler Content 15 %15 %
Water Absorption  0.14 %
@Temperature 23.0 °C
0.14 %
@Temperature 73.4 °F
Equilibrium 50%RH; ISO 62, Similar to
 0.33 %
@Temperature 23.0 °C
0.33 %
@Temperature 73.4 °F
Saturation, immersed; ISO 62, Similar to
Viscosity  52000 cP
@Shear Rate 10000 1/s,
Temperature 260 °C
52000 cP
@Shear Rate 10000 1/s,
Temperature 500 °F
ISO 11443
 69000 cP
@Shear Rate 5000 1/s,
Temperature 260 °C
69000 cP
@Shear Rate 5000 1/s,
Temperature 500 °F
ISO 11443
 71000 cP
@Shear Rate 10000 1/s,
Temperature 250 °C
71000 cP
@Shear Rate 10000 1/s,
Temperature 482 °F
ISO 11443
 93000 cP
@Shear Rate 5000 1/s,
Temperature 250 °C
93000 cP
@Shear Rate 5000 1/s,
Temperature 482 °F
ISO 11443
 98000 cP
@Shear Rate 2000 1/s,
Temperature 260 °C
98000 cP
@Shear Rate 2000 1/s,
Temperature 500 °F
ISO 11443
 100000 cP
@Shear Rate 10000 1/s,
Temperature 240 °C
100000 cP
@Shear Rate 10000 1/s,
Temperature 464 °F
ISO 11443
 128000 cP
@Shear Rate 1000 1/s,
Temperature 260 °C
128000 cP
@Shear Rate 1000 1/s,
Temperature 500 °F
ISO 11443
 131000 cP
@Shear Rate 5000 1/s,
Temperature 240 °C
131000 cP
@Shear Rate 5000 1/s,
Temperature 464 °F
ISO 11443
 133000 cP
@Shear Rate 2000 1/s,
Temperature 250 °C
133000 cP
@Shear Rate 2000 1/s,
Temperature 482 °F
ISO 11443
 166000 cP
@Shear Rate 500 1/s,
Temperature 260 °C
166000 cP
@Shear Rate 500 1/s,
Temperature 500 °F
ISO 11443
 173000 cP
@Shear Rate 1000 1/s,
Temperature 250 °C
173000 cP
@Shear Rate 1000 1/s,
Temperature 482 °F
ISO 11443
 186000 cP
@Shear Rate 2000 1/s,
Temperature 240 °C
186000 cP
@Shear Rate 2000 1/s,
Temperature 464 °F
ISO 11443
 226000 cP
@Shear Rate 500 1/s,
Temperature 250 °C
226000 cP
@Shear Rate 500 1/s,
Temperature 482 °F
ISO 11443
 243000 cP
@Shear Rate 1000 1/s,
Temperature 240 °C
243000 cP
@Shear Rate 1000 1/s,
Temperature 464 °F
ISO 11443
 297000 cP
@Shear Rate 100 1/s,
Temperature 260 °C
297000 cP
@Shear Rate 100 1/s,
Temperature 500 °F
ISO 11443
 317000 cP
@Shear Rate 500 1/s,
Temperature 240 °C
317000 cP
@Shear Rate 500 1/s,
Temperature 464 °F
ISO 11443
 410000 cP
@Shear Rate 100 1/s,
Temperature 250 °C
410000 cP
@Shear Rate 100 1/s,
Temperature 482 °F
ISO 11443
 582000 cP
@Shear Rate 100 1/s,
Temperature 240 °C
582000 cP
@Shear Rate 100 1/s,
Temperature 464 °F
ISO 11443
Linear Mold Shrinkage, Flow 0.0075 cm/cm0.0075 in/inParallel; Annealed; ISO 294-4
 0.0065 cm/cm
@Thickness 2.00 mm
0.0065 in/in
@Thickness 0.0787 in
Parallel; ISO 294-4
Linear Mold Shrinkage, Transverse 0.015 cm/cm0.015 in/inNormal; Annealed; ISO 294-4
 0.0125 cm/cm
@Thickness 2.00 mm
0.0125 in/in
@Thickness 0.0787 in
Normal; ISO 294-4
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break 100 MPa
@Temperature 23.0 °C
14500 psi
@Temperature 73.4 °F
ISO 527
Tensile Stress  5.51 MPa
@Strain 0.250 %,
Temperature 160 °C
799 psi
@Strain 0.250 %,
Temperature 320 °F
ISO 527
 6.79 MPa
@Strain 0.250 %,
Temperature 120 °C
985 psi
@Strain 0.250 %,
Temperature 248 °F
ISO 527
 7.40 MPa
@Strain 0.250 %,
Temperature 100 °C
1070 psi
@Strain 0.250 %,
Temperature 212 °F
ISO 527
 8.45 MPa
@Strain 0.250 %,
Temperature 80.0 °C
1230 psi
@Strain 0.250 %,
Temperature 176 °F
ISO 527
 10.0 MPa
@Strain 0.250 %,
Temperature 60.0 °C
1450 psi
@Strain 0.250 %,
Temperature 140 °F
ISO 527
 10.4 MPa
@Strain 0.500 %,
Temperature 160 °C
1510 psi
@Strain 0.500 %,
Temperature 320 °F
ISO 527
 13.1 MPa
@Strain 0.500 %,
Temperature 120 °C
1900 psi
@Strain 0.500 %,
Temperature 248 °F
ISO 527
 13.1 MPa
@Strain 0.250 %,
Temperature 40.0 °C
1900 psi
@Strain 0.250 %,
Temperature 104 °F
ISO 527
 14.2 MPa
@Strain 0.500 %,
Temperature 100 °C
2060 psi
@Strain 0.500 %,
Temperature 212 °F
ISO 527
 16.0 MPa
@Strain 0.500 %,
Temperature 80.0 °C
2320 psi
@Strain 0.500 %,
Temperature 176 °F
ISO 527
 16.3 MPa
@Strain 0.250 %,
Temperature 23.0 °C
2360 psi
@Strain 0.250 %,
Temperature 73.4 °F
ISO 527
 17.4 MPa
@Strain 0.250 %,
Temperature 0.000 °C
2520 psi
@Strain 0.250 %,
Temperature 32.0 °F
ISO 527
 18.3 MPa
@Strain 1.00 %,
Temperature 160 °C
2650 psi
@Strain 1.00 %,
Temperature 320 °F
ISO 527
 18.6 MPa
@Strain 0.500 %,
Temperature 60.0 °C
2700 psi
@Strain 0.500 %,
Temperature 140 °F
ISO 527
 18.7 MPa
@Strain 0.250 %,
Temperature -20.0 °C
2710 psi
@Strain 0.250 %,
Temperature -4.00 °F
ISO 527
 19.9 MPa
@Strain 0.250 %,
Temperature -40.0 °C
2890 psi
@Strain 0.250 %,
Temperature -40.0 °F
ISO 527
 23.8 MPa
@Strain 1.00 %,
Temperature 120 °C
3450 psi
@Strain 1.00 %,
Temperature 248 °F
ISO 527
 24.1 MPa
@Strain 1.50 %,
Temperature 160 °C
3500 psi
@Strain 1.50 %,
Temperature 320 °F
ISO 527
 26.2 MPa
@Strain 0.500 %,
Temperature 40.0 °C
3800 psi
@Strain 0.500 %,
Temperature 104 °F
ISO 527
 26.2 MPa
@Strain 1.00 %,
Temperature 100 °C
3800 psi
@Strain 1.00 %,
Temperature 212 °F
ISO 527
 28.3 MPa
@Strain 2.00 %,
Temperature 160 °C
4100 psi
@Strain 2.00 %,
Temperature 320 °F
ISO 527
 28.8 MPa
@Strain 1.00 %,
Temperature 80.0 °C
4180 psi
@Strain 1.00 %,
Temperature 176 °F
ISO 527
 31.4 MPa
@Strain 2.50 %,
Temperature 160 °C
4550 psi
@Strain 2.50 %,
Temperature 320 °F
ISO 527
 31.9 MPa
@Strain 1.50 %,
Temperature 120 °C
4630 psi
@Strain 1.50 %,
Temperature 248 °F
ISO 527
 32.5 MPa
@Strain 0.500 %,
Temperature 23.0 °C
4710 psi
@Strain 0.500 %,
Temperature 73.4 °F
ISO 527
 33.1 MPa
@Strain 1.00 %,
Temperature 60.0 °C
4800 psi
@Strain 1.00 %,
Temperature 140 °F
ISO 527
 33.7 MPa
@Strain 3.00 %,
Temperature 160 °C
4890 psi
@Strain 3.00 %,
Temperature 320 °F
ISO 527
 34.2 MPa
@Strain 0.500 %,
Temperature 0.000 °C
4960 psi
@Strain 0.500 %,
Temperature 32.0 °F
ISO 527
 35.4 MPa
@Strain 1.50 %,
Temperature 100 °C
5130 psi
@Strain 1.50 %,
Temperature 212 °F
ISO 527
 35.6 MPa
@Strain 3.50 %,
Temperature 160 °C
5160 psi
@Strain 3.50 %,
Temperature 320 °F
Break; ISO 527
 36.6 MPa
@Strain 0.500 %,
Temperature -20.0 °C
5310 psi
@Strain 0.500 %,
Temperature -4.00 °F
ISO 527
 37.7 MPa
@Strain 2.00 %,
Temperature 120 °C
5470 psi
@Strain 2.00 %,
Temperature 248 °F
ISO 527
 38.7 MPa
@Strain 0.500 %,
Temperature -40.0 °C
5610 psi
@Strain 0.500 %,
Temperature -40.0 °F
ISO 527
 39.0 MPa
@Strain 1.50 %,
Temperature 80.0 °C
5660 psi
@Strain 1.50 %,
Temperature 176 °F
ISO 527
 41.6 MPa
@Strain 2.50 %,
Temperature 120 °C
6030 psi
@Strain 2.50 %,
Temperature 248 °F
ISO 527
 42.0 MPa
@Strain 2.00 %,
Temperature 100 °C
6090 psi
@Strain 2.00 %,
Temperature 212 °F
ISO 527
 44.3 MPa
@Strain 3.00 %,
Temperature 120 °C
6430 psi
@Strain 3.00 %,
Temperature 248 °F
ISO 527
 44.8 MPa
@Strain 1.50 %,
Temperature 60.0 °C
6500 psi
@Strain 1.50 %,
Temperature 140 °F
ISO 527
 46.0 MPa
@Strain 3.50 %,
Temperature 120 °C
6670 psi
@Strain 3.50 %,
Temperature 248 °F
Break; ISO 527
 46.5 MPa
@Strain 2.50 %,
Temperature 100 °C
6740 psi
@Strain 2.50 %,
Temperature 212 °F
ISO 527
 46.6 MPa
@Strain 2.00 %,
Temperature 80.0 °C
6760 psi
@Strain 2.00 %,
Temperature 176 °F
ISO 527
 49.3 MPa
@Strain 3.00 %,
Temperature 100 °C
7150 psi
@Strain 3.00 %,
Temperature 212 °F
ISO 527
 50.2 MPa
@Strain 1.00 %,
Temperature 40.0 °C
7280 psi
@Strain 1.00 %,
Temperature 104 °F
ISO 527
 50.9 MPa
@Strain 3.50 %,
Temperature 100 °C
7380 psi
@Strain 3.50 %,
Temperature 212 °F
Break; ISO 527
 51.7 MPa
@Strain 2.50 %,
Temperature 80.0 °C
7500 psi
@Strain 2.50 %,
Temperature 176 °F
ISO 527
 53.7 MPa
@Strain 2.00 %,
Temperature 60.0 °C
7790 psi
@Strain 2.00 %,
Temperature 140 °F
ISO 527
 54.4 MPa
@Strain 3.00 %,
Temperature 80.0 °C
7890 psi
@Strain 3.00 %,
Temperature 176 °F
ISO 527
 55.0 MPa
@Strain 3.50 %,
Temperature 80.0 °C
7980 psi
@Strain 3.50 %,
Temperature 176 °F
Break; ISO 527
 59.8 MPa
@Strain 2.50 %,
Temperature 60.0 °C
8670 psi
@Strain 2.50 %,
Temperature 140 °F
ISO 527
 60.8 MPa
@Strain 1.00 %,
Temperature 23.0 °C
8820 psi
@Strain 1.00 %,
Temperature 73.4 °F
ISO 527
 63.0 MPa
@Strain 3.00 %,
Temperature 60.0 °C
9140 psi
@Strain 3.00 %,
Temperature 140 °F
ISO 527
 63.5 MPa
@Strain 3.50 %,
Temperature 60.0 °C
9210 psi
@Strain 3.50 %,
Temperature 140 °F
Break; ISO 527
 64.3 MPa
@Strain 1.00 %,
Temperature 0.000 °C
9330 psi
@Strain 1.00 %,
Temperature 32.0 °F
ISO 527
 66.6 MPa
@Strain 1.50 %,
Temperature 40.0 °C
9660 psi
@Strain 1.50 %,
Temperature 104 °F
ISO 527
 68.2 MPa
@Strain 1.00 %,
Temperature -20.0 °C
9890 psi
@Strain 1.00 %,
Temperature -4.00 °F
ISO 527
 71.4 MPa
@Strain 1.00 %,
Temperature -40.0 °C
10400 psi
@Strain 1.00 %,
Temperature -40.0 °F
ISO 527
 75.6 MPa
@Strain 2.00 %,
Temperature 40.0 °C
11000 psi
@Strain 2.00 %,
Temperature 104 °F
ISO 527
 79.6 MPa
@Strain 2.50 %,
Temperature 40.0 °C
11500 psi
@Strain 2.50 %,
Temperature 104 °F
ISO 527
 80.3 MPa
@Strain 1.50 %,
Temperature 23.0 °C
11600 psi
@Strain 1.50 %,
Temperature 73.4 °F
ISO 527
 80.8 MPa
@Strain 3.00 %,
Temperature 40.0 °C
11700 psi
@Strain 3.00 %,
Temperature 104 °F
Break; ISO 527
 87.5 MPa
@Strain 1.50 %,
Temperature 0.000 °C
12700 psi
@Strain 1.50 %,
Temperature 32.0 °F
ISO 527
 90.9 MPa
@Strain 2.00 %,
Temperature 23.0 °C
13200 psi
@Strain 2.00 %,
Temperature 73.4 °F
ISO 527
 92.7 MPa
@Strain 1.50 %,
Temperature -20.0 °C
13400 psi
@Strain 1.50 %,
Temperature -4.00 °F
ISO 527
 94.8 MPa
@Strain 2.50 %,
Temperature 23.0 °C
13700 psi
@Strain 2.50 %,
Temperature 73.4 °F
ISO 527
 94.8 MPa
@Strain 3.00 %,
Temperature 23.0 °C
13700 psi
@Strain 3.00 %,
Temperature 73.4 °F
Break; ISO 527
 96.6 MPa
@Strain 1.50 %,
Temperature -40.0 °C
14000 psi
@Strain 1.50 %,
Temperature -40.0 °F
ISO 527
 103 MPa
@Strain 2.00 %,
Temperature 0.000 °C
14900 psi
@Strain 2.00 %,
Temperature 32.0 °F
ISO 527
 110 MPa
@Strain 2.50 %,
Temperature 0.000 °C
16000 psi
@Strain 2.50 %,
Temperature 32.0 °F
ISO 527
 110 MPa
@Strain 2.00 %,
Temperature -20.0 °C
16000 psi
@Strain 2.00 %,
Temperature -4.00 °F
ISO 527
 112 MPa
@Strain 2.80 %,
Temperature 0.000 °C
16200 psi
@Strain 2.80 %,
Temperature 32.0 °F
Break; ISO 527
 115 MPa
@Strain 2.00 %,
Temperature -40.0 °C
16700 psi
@Strain 2.00 %,
Temperature -40.0 °F
ISO 527
 121 MPa
@Strain 2.50 %,
Temperature -20.0 °C
17500 psi
@Strain 2.50 %,
Temperature -4.00 °F
ISO 527
 124 MPa
@Strain 2.70 %,
Temperature -20.0 °C
18000 psi
@Strain 2.70 %,
Temperature -4.00 °F
Break; ISO 527
 126 MPa
@Strain 2.50 %,
Temperature -40.0 °C
18300 psi
@Strain 2.50 %,
Temperature -40.0 °F
ISO 527
 130 MPa
@Strain 2.70 %,
Temperature -40.0 °C
18900 psi
@Strain 2.70 %,
Temperature -40.0 °F
Break; ISO 527
Elongation at Break 3.4 %
@Temperature 23.0 °C
3.4 %
@Temperature 73.4 °F
ISO 527
Tensile Modulus 7.20 GPa
@Temperature 23.0 °C
1040 ksi
@Temperature 73.4 °F
ISO 527
Flexural Strength 155 MPa
@Temperature 23.0 °C
22500 psi
@Temperature 73.4 °F
ISO 178
Shear Modulus  0.279 GPa
@Temperature 200 °C
40.5 ksi
@Temperature 392 °F
ISO 6721
 0.351 GPa
@Temperature 190 °C
50.9 ksi
@Temperature 374 °F
ISO 6721
 0.396 GPa
@Temperature 180 °C
57.4 ksi
@Temperature 356 °F
ISO 6721
 0.428 GPa
@Temperature 170 °C
62.1 ksi
@Temperature 338 °F
ISO 6721
 0.464 GPa
@Temperature 160 °C
67.3 ksi
@Temperature 320 °F
ISO 6721
 0.518 GPa
@Temperature 150 °C
75.1 ksi
@Temperature 302 °F
ISO 6721
 0.557 GPa
@Temperature 140 °C
80.8 ksi
@Temperature 284 °F
ISO 6721
 0.591 GPa
@Temperature 130 °C
85.7 ksi
@Temperature 266 °F
ISO 6721
 0.623 GPa
@Temperature 120 °C
90.4 ksi
@Temperature 248 °F
ISO 6721
 0.655 GPa
@Temperature 110 °C
95.0 ksi
@Temperature 230 °F
ISO 6721
 0.691 GPa
@Temperature 100 °C
100 ksi
@Temperature 212 °F
ISO 6721
 0.734 GPa
@Temperature 90.0 °C
106 ksi
@Temperature 194 °F
ISO 6721
 0.798 GPa
@Temperature 80.0 °C
116 ksi
@Temperature 176 °F
ISO 6721
 0.896 GPa
@Temperature 70.0 °C
130 ksi
@Temperature 158 °F
ISO 6721
 1.05 GPa
@Temperature 60.0 °C
152 ksi
@Temperature 140 °F
ISO 6721
 1.27 GPa
@Temperature 50.0 °C
184 ksi
@Temperature 122 °F
ISO 6721
 1.50 GPa
@Temperature 40.0 °C
218 ksi
@Temperature 104 °F
ISO 6721
 1.62 GPa
@Temperature 30.0 °C
235 ksi
@Temperature 86.0 °F
ISO 6721
 1.67 GPa
@Temperature 20.0 °C
242 ksi
@Temperature 68.0 °F
ISO 6721
 1.71 GPa
@Temperature 10.0 °C
248 ksi
@Temperature 50.0 °F
ISO 6721
 1.74 GPa
@Temperature 0.000 °C
252 ksi
@Temperature 32.0 °F
ISO 6721
 1.77 GPa
@Temperature -10.0 °C
257 ksi
@Temperature 14.0 °F
ISO 6721
 1.82 GPa
@Temperature -20.0 °C
264 ksi
@Temperature -4.00 °F
ISO 6721
 1.87 GPa
@Temperature -30.0 °C
271 ksi
@Temperature -22.0 °F
ISO 6721
 1.92 GPa
@Temperature -40.0 °C
278 ksi
@Temperature -40.0 °F
ISO 6721
 1.96 GPa
@Temperature -50.0 °C
284 ksi
@Temperature -58.0 °F
ISO 6721
Izod Impact, Notched (ISO)  6.00 kJ/m²
@Temperature -30.0 °C
2.86 ft-lb/in²
@Temperature -22.0 °F
ISO 180/1A
 7.00 kJ/m²
@Temperature 23.0 °C
3.33 ft-lb/in²
@Temperature 73.4 °F
ISO 180/1A
Izod Impact, Unnotched (ISO)  32.0 kJ/m²
@Temperature -30.0 °C
15.2 ft-lb/in²
@Temperature -22.0 °F
ISO 180/1U
 33.0 kJ/m²
@Temperature 23.0 °C
15.7 ft-lb/in²
@Temperature 73.4 °F
ISO 180/1U
Charpy Impact Unnotched  4.40 J/cm²
@Temperature -30.0 °C
20.9 ft-lb/in²
@Temperature -22.0 °F
ISO 179/1eU
 5.30 J/cm²
@Temperature 23.0 °C
25.2 ft-lb/in²
@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched  0.710 J/cm²
@Temperature -30.0 °C
3.38 ft-lb/in²
@Temperature -22.0 °F
ISO 179/1eA
 0.800 J/cm²
@Temperature 23.0 °C
3.81 ft-lb/in²
@Temperature 73.4 °F
ISO 179/1eA
Tensile Creep Modulus, 1 hour 6000 MPa
@Temperature 23.0 °C
870000 psi
@Temperature 73.4 °F
ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C
0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F
1h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C
0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F
10h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.180 %,
Temperature 23.0 °C
1450 psi
@Strain 0.180 %,
Temperature 73.4 °F
10h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.167 %,
Temperature 23.0 °C
1450 psi
@Strain 0.167 %,
Temperature 73.4 °F
1h; Isochronous; ISO 899
 20.0 MPa
@Strain 0.334 %,
Temperature 23.0 °C
2900 psi
@Strain 0.334 %,
Temperature 73.4 °F
1h; Isochronous; ISO 899
 20.0 MPa
@Strain 0.360 %,
Temperature 23.0 °C
2900 psi
@Strain 0.360 %,
Temperature 73.4 °F
10h; Isochronous; ISO 899
 30.0 MPa
@Strain 0.500 %,
Temperature 23.0 °C
4350 psi
@Strain 0.500 %,
Temperature 73.4 °F
1h; Isochronous; ISO 899
 30.0 MPa
@Strain 0.540 %,
Temperature 23.0 °C
4350 psi
@Strain 0.540 %,
Temperature 73.4 °F
10h; Isochronous; ISO 899
 40.0 MPa
@Strain 0.720 %,
Temperature 23.0 °C
5800 psi
@Strain 0.720 %,
Temperature 73.4 °F
10h; Isochronous; ISO 899
 40.0 MPa
@Strain 0.670 %,
Temperature 23.0 °C
5800 psi
@Strain 0.670 %,
Temperature 73.4 °F
1h; Isochronous; ISO 899
 50.0 MPa
@Strain 0.900 %,
Temperature 23.0 °C
7250 psi
@Strain 0.900 %,
Temperature 73.4 °F
10h; Isochronous; ISO 899
 50.0 MPa
@Strain 0.850 %,
Temperature 23.0 °C
7250 psi
@Strain 0.850 %,
Temperature 73.4 °F
1h; Isochronous; ISO 899
 60.0 MPa
@Strain 1.03 %,
Temperature 23.0 °C
8700 psi
@Strain 1.03 %,
Temperature 73.4 °F
1h; Isochronous; ISO 899
 60.0 MPa
@Strain 1.18 %,
Temperature 23.0 °C
8700 psi
@Strain 1.18 %,
Temperature 73.4 °F
10h; Isochronous; ISO 899
 70.0 MPa
@Strain 1.64 %,
Temperature 23.0 °C
10200 psi
@Strain 1.64 %,
Temperature 73.4 °F
10h; Break; Isochronous; ISO 899
 70.0 MPa
@Strain 1.35 %,
Temperature 23.0 °C
10200 psi
@Strain 1.35 %,
Temperature 73.4 °F
1h; Break; Isochronous; ISO 899
Tensile Creep Modulus, 1000 hours 4800 MPa
@Temperature 23.0 °C
696000 psi
@Temperature 73.4 °F
ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C
0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F
1000h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C
0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F
100h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.200 %,
Temperature 23.0 °C
1450 psi
@Strain 0.200 %,
Temperature 73.4 °F
100h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.210 %,
Temperature 23.0 °C
1450 psi
@Strain 0.210 %,
Temperature 73.4 °F
1000h; Isochronous; ISO 899
 20.0 MPa
@Strain 0.420 %,
Temperature 23.0 °C
2900 psi
@Strain 0.420 %,
Temperature 73.4 °F
1000h; Isochronous; ISO 899
 20.0 MPa
@Strain 0.400 %,
Temperature 23.0 °C
2900 psi
@Strain 0.400 %,
Temperature 73.4 °F
100h; Isochronous; ISO 899
 30.0 MPa
@Strain 0.630 %,
Temperature 23.0 °C
4350 psi
@Strain 0.630 %,
Temperature 73.4 °F
1000h; Isochronous; ISO 899
 30.0 MPa
@Strain 0.600 %,
Temperature 23.0 °C
4350 psi
@Strain 0.600 %,
Temperature 73.4 °F
100h; Isochronous; ISO 899
 40.0 MPa
@Strain 0.800 %,
Temperature 23.0 °C
5800 psi
@Strain 0.800 %,
Temperature 73.4 °F
100h; Isochronous; ISO 899
 40.0 MPa
@Strain 0.880 %,
Temperature 23.0 °C
5800 psi
@Strain 0.880 %,
Temperature 73.4 °F
1000h; Isochronous; ISO 899
 50.0 MPa
@Strain 1.02 %,
Temperature 23.0 °C
7250 psi
@Strain 1.02 %,
Temperature 73.4 °F
100h; Isochronous; ISO 899
 50.0 MPa
@Strain 1.19 %,
Temperature 23.0 °C
7250 psi
@Strain 1.19 %,
Temperature 73.4 °F
1000h; Isochronous; ISO 899
 60.0 MPa
@Strain 1.64 %,
Temperature 23.0 °C
8700 psi
@Strain 1.64 %,
Temperature 73.4 °F
1000h; Isochronous; ISO 899
 60.0 MPa
@Strain 1.35 %,
Temperature 23.0 °C
8700 psi
@Strain 1.35 %,
Temperature 73.4 °F
100h; Isochronous; ISO 899
 70.0 MPa
@Strain 1.93 %,
Temperature 23.0 °C
10200 psi
@Strain 1.93 %,
Temperature 73.4 °F
100h; Break; Isochronous; ISO 899
 70.0 MPa
@Strain 2.34 %,
Temperature 23.0 °C
10200 psi
@Strain 2.34 %,
Temperature 73.4 °F
1000h; Break; Isochronous; ISO 899
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity >= 1.00e+15 ohm-cm
@Temperature 23.0 °C
>= 1.00e+15 ohm-cm
@Temperature 73.4 °F
IEC 60093
Surface Resistance 1.00e+15 ohm
@Temperature 23.0 °C
1.00e+15 ohm
@Temperature 73.4 °F
IEC 60093
Dielectric Constant  3.5
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C
3.5
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F
IEC 60250
 3.7
@Frequency 100 Hz,
Temperature 23.0 °C
3.7
@Frequency 100 Hz,
Temperature 73.4 °F
IEC 60250
Dielectric Strength 28.0 kV/mm
@Thickness 1.00 mm,
Temperature 23.0 °C
711 kV/in
@Thickness 0.0394 in,
Temperature 73.4 °F
IEC 60243-1
 17.0 kV/mm
@Thickness 2.00 mm,
Time 20.0 sec
432 kV/in
@Thickness 0.0787 in,
Time 0.00556 hour
IEC 60243-1
Dissipation Factor  0.0030
@Frequency 100 Hz,
Temperature 23.0 °C
0.0030
@Frequency 100 Hz,
Temperature 73.4 °F
IEC 60250
 0.017
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C
0.017
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F
IEC 60250
Comparative Tracking Index  175 V
@Temperature 23.0 °C
175 V
@Temperature 73.4 °F
UL 746A
 250 V
@Temperature 23.0 °C
250 V
@Temperature 73.4 °F
IEC 60112
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow  500 µm/m-°C
@Temperature 23.0 - 55.0 °C
278 µin/in-°F
@Temperature 73.4 - 131 °F
ASTM E 831
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C
278 µin/in-°F
@Temperature 73.4 - 131 °F
ISO 11359-1/-2
CTE, linear, Transverse to Flow  110 µm/m-°C
@Temperature 23.0 - 55.0 °C
61.1 µin/in-°F
@Temperature 73.4 - 131 °F
ASTM E 831
 110 µm/m-°C
@Temperature 23.0 - 55.0 °C
61.1 µin/in-°F
@Temperature 73.4 - 131 °F
ISO 11359-1/-2
Deflection Temperature at 0.46 MPa (66 psi) 218 °C424 °FISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 203 °C397 °FISO 75-1/-2
Deflection Temperature at 5.0 MPa 168 °C334 °F4x100x100mm plaque; ISO 75-1/-2
Deflection Temperature at 8.0 MPa 116 °C241 °FISO 75-1/-2
UL RTI, Electrical  140 °C
@Thickness 1.50 mm
284 °F
@Thickness 0.0591 in
UL 746B
 140 °C
@Thickness 3.00 mm
284 °F
@Thickness 0.118 in
UL 746B
 140 °C
@Thickness 6.00 mm
284 °F
@Thickness 0.236 in
UL 746B
UL RTI, Mechanical with Impact  130 °C
@Thickness 6.00 mm
266 °F
@Thickness 0.236 in
UL 746B
 130 °C
@Thickness 3.00 mm
266 °F
@Thickness 0.118 in
UL 746B
 130 °C
@Thickness 1.50 mm
266 °F
@Thickness 0.0591 in
UL 746B
UL RTI, Mechanical without Impact  140 °C
@Thickness 3.00 mm
284 °F
@Thickness 0.118 in
UL 746B
 140 °C
@Thickness 6.00 mm
284 °F
@Thickness 0.236 in
UL 746B
 140 °C
@Thickness 1.50 mm
284 °F
@Thickness 0.0591 in
UL 746B
Flammability, UL94  V-0
@Thickness 1.50 mm
V-0
@Thickness 0.0591 in
IEC 60695-11-10
 V-0
@Thickness 3.00 mm
V-0
@Thickness 0.118 in
IEC 60695-11-10
 V-0
@Thickness 6.00 mm
V-0
@Thickness 0.236 in
IEC 60695-11-10
 V-0
@Thickness 6.00 mm
V-0
@Thickness 0.236 in
UL94
 V-0
@Thickness 1.50 mm
V-0
@Thickness 0.0591 in
UL94
 V-0
@Thickness 3.00 mm
V-0
@Thickness 0.118 in
UL94
Oxygen Index 31 %31 %ISO 4589-1/-2
Glow Wire Test 960 °C
@Thickness 3.00 mm
1760 °F
@Thickness 0.118 in
IEC 60695-2-12
 
Processing PropertiesMetricEnglishComments
Melt Temperature 225 °C437 °F10°C/min; ISO 11357-1/-3
 250 °C482 °FOptimum
 240 - 260 °C464 - 500 °F
Mold Temperature 80.0 °C176 °Foptimum
 30.0 - 130 °C86.0 - 266 °F
Drying Temperature 110 - 130 °C230 - 266 °F
Dry Time 2.00 - 4.00 hour2.00 - 4.00 hour
Moisture Content <= 0.040 %<= 0.040 %
 
Descriptive Properties
AppearanceNatural Color
Contains Flame RetardantYes
Drying RecommendedYes
FeaturesFlame Retardant
FillerGlass Fiber Reinforcement
FormsPellets
GenericPBT
Material StatusPreliminary Data
Part Marking Code>PBT-GF15FR(17)<ISO 11469
Polymer FamilyPolyester
Polymer TypePBT
Processing MethodInjection Molding
 Injection Molding
Product CategoryFlame Retardant Resins
 Glass Reinforced Resins
Region Available - GlobalYes
Resin IdentificationPBT-GF15FR(17)ISO 1043
RoHS ComplianceContact Manufacturer
Ultrasonic WeldableYes
UsesAutomotive Applications
 Electrical/Electronic Applications

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-38099.html

免责声明: 本文 DuPont Performance Polymers Crastin® SK642FR NC010 PBT 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4