- 密度 [g/cm3]: 1.53
- 缺口冲击强度: 9.0
- 弯曲模量 [MPa]: 9.70
- 热变形温度 [℃]: 222.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.53 g/cc | 0.0553 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.16 % | 0.16 % | 23°C/50%RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.012 cm/cm | 0.0070 - 0.012 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 150 MPa | 21800 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 2.6 % | 2.6 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 10.4 GPa | 1510 ksi | 1mm/min; ISO 527-2/1A |
| Flexural Strength | 220 MPa | 31900 psi | ISO 178 |
| Flexural Modulus | 9.70 GPa | 1410 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 45.0 kJ/m² @Temperature 23.0 °C | 21.4 ft-lb/in² @Temperature 73.4 °F | ISO 180/1U |
| Charpy Impact Unnotched | 4.40 J/cm² | 20.9 ft-lb/in² | ISO 179/1eU |
| 3.90 J/cm² @Temperature 30.0 °C | 18.6 ft-lb/in² @Temperature 86.0 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | ISO 179/1eA |
| 0.910 J/cm² @Temperature 30.0 °C | 4.33 ft-lb/in² @Temperature 86.0 °F | ISO 179/1eA | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 2.00e+15 ohm-cm | 2.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 2.00e+15 ohm | 2.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 2.8 @Frequency 100 Hz | 2.8 @Frequency 100 Hz | IEC 60250 |
| 3.2 @Frequency 1.00e+6 Hz | 3.2 @Frequency 1.00e+6 Hz | IEC 60250 | |
| Dielectric Strength | 22.0 kV/mm | 559 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.014 @Frequency 1.00e+6 Hz | 0.014 @Frequency 1.00e+6 Hz | IEC 60250 |
| Comparative Tracking Index | 254 V | 254 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 19.0 µm/m-°C | 10.6 µin/in-°F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 100 µm/m-°C | 55.6 µin/in-°F | ISO 11359-2 |
| Melting Point | 225 °C | 437 °F | ISO 11357-1,-2,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 222 °C | 432 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75-1, -2 |
| Flammability, UL94 | HB | HB | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | hopper |
| 65.0 - 93.0 °C | 149 - 199 °F | cavity | |
| Feed Temperature | 230 - 240 °C | 446 - 464 °F | |
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |
| Zone 2 | 235 - 250 °C | 455 - 482 °F | |
| Zone 3 | 235 - 250 °C | 455 - 482 °F | |
| Zone 4 | 240 - 260 °C | 464 - 500 °F | |
| Die Temperature | 250 - 260 °C | 482 - 500 °F | |
| Melt Temperature | 235 - 260 °C | 455 - 500 °F | |
| Hot-Working Temperature | 250 - 260 °C | 482 - 500 °F | |