- 熔体流动速率 [g/10min]: 5.5
- 密度 [g/cm3]: 1.47
- 吸水率 [%]: 0.11
- 缺口冲击强度: 2.19
- 拉伸强度 [MPa]: 82.7
- 弯曲模量 [MPa]: 6.70
- 热变形温度 [℃]: 214.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.47 g/cc | 1.47 g/cc | ASTM D792 | ||
| Density | 1.47 g/cc | 0.0531 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.110 % | 0.110 % | 24hr immersion; ASTM D570 | ||
| Moisture Absorption | 0.200 % | 0.200 % | 23°C/50%RH; ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.00300 - 0.00500 cm/cm | 0.00300 - 0.00500 in/in | ASTM D955 | ||
| 0.00300 - 0.00500 cm/cm | 0.00300 - 0.00500 in/in | ISO 294-4 | |||
| Linear Mold Shrinkage, Transverse | 0.0120 - 0.0140 cm/cm | 0.0120 - 0.0140 in/in | ISO 294-4 | ||
| Melt Flow | 5.50 g/10 min @Load 5.00 kg, Temperature 250 °C | 5.50 g/10 min @Load 11.0 lb, Temperature 482 °F | (MVR) cm³/10min; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 112 | 112 | ISO 2039-2 | ||
| Tensile Strength at Break | 80.0 MPa | 11600 psi | 5mm/min; ISO 527-2/1A | ||
| Tensile Strength, Yield | 82.7 MPa | 12000 psi | ASTM D638 | ||
| Elongation at Break | 3.50 % | 3.50 % | 5mm/min; ISO 527-2/1A | ||
| 4.50 % @Temperature 22.8 °C | 4.50 % @Temperature 73.0 °F | ASTM D638 | |||
| Tensile Modulus | 7.00 GPa | 1020 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 130 MPa | 18900 psi | ISO 178 | ||
| 131 MPa | 19000 psi | ASTM D790 | |||
| Flexural Modulus | 6.70 GPa | 972 ksi | ISO 178 | ||
| 6.38 GPa @Temperature 22.8 °C | 925 ksi @Temperature 73.0 °F | ASTM D790 | |||
| Izod Impact, Notched | 2.19 J/cm | 4.10 ft-lb/in | ASTM D256 | ||
| 0.961 J/cm @Temperature -28.9 °C | 1.80 ft-lb/in @Temperature -20.0 °F | ASTM D256 | |||
| Izod Impact, Notched (ISO) | 21.0 kJ/m² | 9.99 ft-lb/in² | ISO 180/1A | ||
| 10.0 kJ/m² @Temperature -30.0 °C | 4.76 ft-lb/in² @Temperature -22.0 °F | ISO 180/1A | |||
| Charpy Impact Unnotched | 7.00 J/cm² | 33.3 ft-lb/in² | ISO 179/1eU | ||
| 7.00 J/cm² @Temperature -30.0 °C | 33.3 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 2.00 J/cm² | 9.52 ft-lb/in² | ISO 179/1eA | ||
| 1.00 J/cm² @Temperature -30.0 °C | 4.76 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | IEC 60093 | ||
| 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 | |||
| Surface Resistance | >= 1.00e+14 ohm | >= 1.00e+14 ohm | IEC 60093 | ||
| Dielectric Constant | 3.90 @Frequency 1000 Hz | 3.90 @Frequency 1000 Hz | ASTM D150 | ||
| 4.30 @Frequency 1.00e+6 Hz | 4.30 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| 4.90 @Frequency 100 Hz | 4.90 @Frequency 100 Hz | IEC 60250 | |||
| Dielectric Strength | 33.0 kV/mm | 838 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.00500 @Frequency 1000 Hz | 0.00500 @Frequency 1000 Hz | ASTM D150 | ||
| 0.00700 @Frequency 100 Hz | 0.00700 @Frequency 100 Hz | IEC 60250 | |||
| 0.0260 @Frequency 1.00e+6 Hz | 0.0260 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Arc Resistance | 120 sec | 120 sec | ASTM D495 | ||
| Comparative Tracking Index | 425 V | 425 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 15.0 µm/m-°C | 8.33 µin/in-°F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 127 µm/m-°C | 70.6 µin/in-°F | ISO 11359-2 | ||
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| 225 °C | 437 °F | ASTM D3418 | |||
| Transformation Temperature, Tg | 60.0 °C | 140 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | ASTM D648 | ||
| 218 °C | 424 °F | ISO 75-1, -2 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 175 °C | 347 °F | ISO 75-1, -2 | ||
| 190 °C | 374 °F | ASTM D648 | |||
| Vicat Softening Point | 190 °C | 374 °F | B50 (50°C/h 50N); ISO 306 | ||
| Flammability, UL94 | HB | HB | UL94 | ||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | UL94 | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |||
| 65.0 - 96.0 °C | 149 - 205 °F | Cavity temperature | |||
| Feed Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Rear Barrel Temperature | 230 - 250 °C | 446 - 482 °F | |||
| Middle Barrel Temperature | 235 - 255 °C | 455 - 491 °F | |||
| Front Barrel Temperature | 240 - 260 °C | 464 - 500 °F | |||
| Nozzle Temperature | 240 - 265 °C | 464 - 509 °F | |||
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |||
| Zone 2 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 3 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 4 | 240 - 260 °C | 464 - 500 °F | |||
| Die Temperature | 240 - 260 °C | 464 - 500 °F | |||
| Melt Temperature | 235 - 260 °C | 455 - 500 °F | |||
| 240 - 265 °C | 464 - 509 °F | ||||
| 260 °C | 500 °F | Injection molding; ISO 294 | |||
| Mold Temperature | 37.8 - 93.3 °C | 100 - 200 °F | |||
| 82.0 °C | 180 °F | Injection molding; ISO 294 | |||
| Injection Velocity | 300 mm/sec | 11.8 in/sec | ISO 294 | ||
| Drying Temperature | 120 - 130 °C | 248 - 266 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | |||
| Moisture Content | 0.0200 % | 0.0200 % | Necessary low maximum residual | ||
| Hold Pressure | 86.0 MPa | 12500 psi | ISO 294 | ||
| Back Pressure | 0.000 - 0.345 MPa | 0.000 - 50.0 psi | |||
| Hot-Working Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Descriptive Properties | |||||
| Injection molding | Yes | ||||
| Injection speed | medium-fast | ||||
| Longer pre-drying times/storage | 100° C | <= 60 h | |||
| Processing conditions | ISO 7792-2 | ||||
| Processing Notes | Fast Injection Speed | ||||
| Screw Speed - Moderate | |||||