- 密度 [g/cm3]: 1.46
- 缺口冲击强度: 13.6
- 弯曲模量 [MPa]: 7.30
- 热变形温度 [℃]: 206.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in³ | ISO 1183 | ||
| Moisture Absorption at Equilibrium | 0.16 % | 0.16 % | 23°C/50%RH; ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.00 - 0.0050 cm/cm | 0.00 - 0.0050 in/in | ISO 294-4 | ||
| 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | ASTM D955 | |||
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm | 0.0060 in/in | ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 100 MPa | 14500 psi | 5mm/min; ISO 527-2/1A | ||
| Elongation at Break | 3.9 % | 3.9 % | 5mm/min; ISO 527-2/1A | ||
| Tensile Modulus | 7.60 GPa | 1100 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 160 MPa | 23200 psi | ISO 178 | ||
| Flexural Modulus | 7.30 GPa | 1060 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 13.6 kJ/m² | 6.47 ft-lb/in² | ISO 180/1A | ||
| Charpy Impact Unnotched | 3.00 J/cm² | 14.3 ft-lb/in² | ISO 179/1eU | ||
| 4.60 J/cm² @Temperature 30.0 °C | 21.9 ft-lb/in² @Temperature 86.0 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 1.32 J/cm² | 6.28 ft-lb/in² | ISO 179/1eA | ||
| 0.940 J/cm² @Temperature 30.0 °C | 4.47 ft-lb/in² @Temperature 86.0 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 2.00e+14 ohm-cm | 2.00e+14 ohm-cm | IEC 60093 | ||
| 1.30e+16 ohm-cm | 1.30e+16 ohm-cm | ASTM D257 | |||
| Surface Resistance | 8.60e+16 ohm | 8.60e+16 ohm | ASTM D257 | ||
| 2.00e+17 ohm | 2.00e+17 ohm | IEC 60093 | |||
| Dielectric Constant | 2.9 @Frequency 100 Hz | 2.9 @Frequency 100 Hz | IEC 60250 | ||
| 3.3 @Frequency 1.00e+6 Hz | 3.3 @Frequency 1.00e+6 Hz | ASTM D150 | |||
| 3.4 @Frequency 1.00e+6 Hz | 3.4 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Dielectric Strength | 19.3 kV/mm | 489 kV/in | short term; ASTM D149 | ||
| 32.0 kV/mm | 813 kV/in | IEC 60243-1 | |||
| Dissipation Factor | 0.015 @Frequency 1.00e+6 Hz | 0.015 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 0.016 @Frequency 1.00e+6 Hz | 0.016 @Frequency 1.00e+6 Hz | ASTM D150 | |||
| Arc Resistance | 122 sec | 122 sec | ASTM D495 | ||
| Comparative Tracking Index | 375 V | 375 V | IEC 60112 | ||
| 573 V | 573 V | ASTM D3638 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 21.0 µm/m-°C | 11.7 µin/in-°F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 123 µm/m-°C | 68.3 µin/in-°F | ISO 11359-2 | ||
| Melting Point | 225 °C | 437 °F | ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 206 °C | 403 °F | ISO 75-1, -2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 184 °C | 363 °F | ISO 75-1, -2 | ||
| Glass Transition Temp, Tg | 19.0 °C | 66.2 °F | ISO 11357-1,-2,-3 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | hopper | ||
| 65.0 - 93.0 °C | 149 - 199 °F | cavity | |||
| Feed Temperature | 230 - 245 °C | 446 - 473 °F | |||
| Zone 1 | 230 - 245 °C | 446 - 473 °F | |||
| Zone 2 | 240 - 250 °C | 464 - 482 °F | |||
| Zone 3 | 240 - 250 °C | 464 - 482 °F | |||
| Zone 4 | 245 - 260 °C | 473 - 500 °F | |||
| Die Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Melt Temperature | 240 - 260 °C | 464 - 500 °F | |||
| Drying Temperature | 120 - 130 °C | 248 - 266 °F | |||
| Dry Time | 4 hour | 4 hour | |||
| Moisture Content | 0.020 % | 0.020 % | Necessary low maximum | ||
| Hot-Working Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Descriptive Properties | |||||
| Injection molding | Yes | ||||
| Injection speed | medium-fast | ||||