- 密度 [g/cm3]: 1.45
- 缺口冲击强度: 0.694
- 弯曲模量 [MPa]: 5.50
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0080 cm/cm | 0.0040 - 0.0080 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 105 MPa | 15200 psi | 5mm/min; ISO 527-2/1A |
| 96.5 MPa @Temperature 22.8 °C | 14000 psi @Temperature 73.0 °F | ASTM D638 | |
| Elongation at Break | 4.0 % | 4.0 % | 5mm/min; ISO 527-2/1A |
| 4.0 % @Temperature 22.8 °C | 4.0 % @Temperature 73.0 °F | ASTM D638 | |
| Tensile Modulus | 6.25 GPa | 906 ksi | 1mm/min; ISO 527-2/1A |
| Flexural Strength | 170 MPa | 24700 psi | ISO 178 |
| 172 MPa @Temperature 22.8 °C | 25000 psi @Temperature 73.0 °F | ASTM D790 | |
| Flexural Modulus | 5.50 GPa | 798 ksi | ISO 178 |
| 5.52 GPa @Temperature 22.8 °C | 800 ksi @Temperature 73.0 °F | ASTM D790 | |
| Izod Impact, Notched | 0.694 J/cm @Temperature 22.8 °C | 1.30 ft-lb/in @Temperature 73.0 °F | ASTM D256 |
| Izod Impact, Notched (ISO) | 7.50 kJ/m² | 3.57 ft-lb/in² | ISO 180/1A |
| Charpy Impact, Notched | 0.630 J/cm² | 3.00 ft-lb/in² | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Arc Resistance | 130 sec | 130 sec | ASTM D495 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 31.0 µm/m-°C | 17.2 µin/in-°F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 120 µm/m-°C | 66.7 µin/in-°F | ISO 11359-2 |
| Flammability, UL94 | HB | HB | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | hopper |
| 65.0 - 93.0 °C | 149 - 199 °F | cavity | |
| Feed Temperature | 230 - 240 °C | 446 - 464 °F | |
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |
| Zone 2 | 235 - 250 °C | 455 - 482 °F | |
| Zone 3 | 235 - 250 °C | 455 - 482 °F | |
| Zone 4 | 240 - 260 °C | 464 - 500 °F | |
| Die Temperature | 250 - 260 °C | 482 - 500 °F | |
| Melt Temperature | 235 - 260 °C | 455 - 500 °F | |
| Hot-Working Temperature | 250 - 260 °C | 482 - 500 °F | |