- 密度 [g/cm3]: 1.41
- 缺口冲击强度: 5.3
- 弯曲模量 [MPa]: 5.39
- 热变形温度 [℃]: 220.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.41 g/cc | 1.41 g/cc | ASTM D792 | ||
| Density | 1.41 g/cc | 0.0509 lb/in³ | ISO 1183 | ||
| Moisture Absorption at Equilibrium | 0.17 % | 0.17 % | 23°C/50%RH; ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 90 | 90 | ISO 2039-2 | ||
| Tensile Strength at Break | 100 MPa | 14500 psi | 5mm/min; ISO 527-2/1A | ||
| Elongation at Break | 3.5 % | 3.5 % | 5mm/min; ISO 527-2/1A | ||
| Tensile Modulus | 5.80 GPa | 841 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 149 MPa | 21600 psi | ISO 178 | ||
| Flexural Modulus | 5.39 GPa | 782 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 5.30 kJ/m² | 2.52 ft-lb/in² | ISO 180/1A | ||
| Izod Impact, Unnotched (ISO) | 17.0 kJ/m² @Temperature 23.0 °C | 8.09 ft-lb/in² @Temperature 73.4 °F | ISO 180/1U | ||
| Charpy Impact Unnotched | 2.00 J/cm² | 9.52 ft-lb/in² | ISO 179/1eU | ||
| 2.00 J/cm² @Temperature 30.0 °C | 9.52 ft-lb/in² @Temperature 86.0 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.550 J/cm² | 2.62 ft-lb/in² | ISO 179/1eA | ||
| 0.500 J/cm² @Temperature 30.0 °C | 2.38 ft-lb/in² @Temperature 86.0 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 | ||
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 | ||
| Dielectric Constant | 3.8 @Frequency 1.00e+6 Hz | 3.8 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 4.2 @Frequency 50.0 Hz | 4.2 @Frequency 50.0 Hz | IEC 60250 | |||
| Dielectric Strength | 29.0 kV/mm | 737 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.0016 @Frequency 50.0 Hz | 0.0016 @Frequency 50.0 Hz | IEC 60250 | ||
| 0.020 @Frequency 1.00e+6 Hz | 0.020 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Comparative Tracking Index | 350 V | 350 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 225 °C | 437 °F | ISO 11357-1,-2,-3 | ||
| 225 °C | 437 °F | ASTM D3418 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75-1, -2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C | 383 °F | ISO 75-1, -2 | ||
| Deflection Temperature at 8.0 MPa | 90.0 °C | 194 °F | ISO 75-1, -2 | ||
| Vicat Softening Point | 220 °C | 428 °F | B50 (50°C/h 50N); ISO 306 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | hopper | ||
| 65.0 - 93.0 °C | 149 - 199 °F | cavity | |||
| Feed Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |||
| Zone 2 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 3 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 4 | 240 - 260 °C | 464 - 500 °F | |||
| Die Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Melt Temperature | 235 - 260 °C | 455 - 500 °F | |||
| Drying Temperature | 120 - 130 °C | 248 - 266 °F | |||
| Dry Time | 4 hour | 4 hour | |||
| Moisture Content | 0.020 % | 0.020 % | Necessary low maximum | ||
| Hot-Working Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Descriptive Properties | |||||
| Injection molding | Yes | ||||
| Injection speed | medium-fast | ||||