- 密度 [g/cm3]: 1.81
- 缺口冲击强度: 0.694
- 弯曲模量 [MPa]: 10.775
- 热变形温度 [℃]: 222.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.81 g/cc | 1.81 g/cc | ASTM D792 |
| Density | 1.81 g/cc | 0.0654 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0030 cm/cm | 0.0020 - 0.0030 in/in | ISO 294-4 |
| 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0055 - 0.0075 cm/cm | 0.0055 - 0.0075 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 84.0 MPa | 12200 psi | 5mm/min; ISO 527-2/1A |
| 82.0 MPa @Temperature 22.8 °C | 11900 psi @Temperature 73.0 °F | ASTM D638 | |
| Elongation at Break | 1.5 % | 1.5 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 11.0 GPa | 1600 ksi | 1mm/min; ISO 527-2/1A |
| Flexural Strength | 135 MPa | 19600 psi | ISO 178 |
| 134 MPa @Temperature 22.8 °C | 19500 psi @Temperature 73.0 °F | ASTM D790 | |
| Flexural Modulus | 10.775 GPa | 1562.8 ksi | ISO 178 |
| 11.33 GPa @Temperature 22.8 °C | 1643 ksi @Temperature 73.0 °F | ASTM D790 | |
| Izod Impact, Notched | 0.694 J/cm @Temperature 22.8 °C | 1.30 ft-lb/in @Temperature 73.0 °F | ASTM D256 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 33.0 kJ/m² @Temperature 23.0 °C | 15.7 ft-lb/in² @Temperature 73.4 °F | ISO 180/1U |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| Dielectric Strength | 26.0 kV/mm | 660 kV/in | short term; ASTM D149 |
| Arc Resistance | 136 sec | 136 sec | ASTM D495 |
| Comparative Tracking Index | 600 V | 600 V | ASTM D3638 |
| 600 V | 600 V | IEC 60112 | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 222 °C | 432 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 201 °C | 394 °F | ISO 75-1, -2 |
| Flammability, UL94 | V-0 | V-0 | |