- 密度 [g/cm3]: 1.31
- 缺口冲击强度: 5.0
- 拉伸强度 [MPa]: 60.0
- 弯曲模量 [MPa]: 2.50
- 热变形温度 [℃]: 150.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | 50 mm/min; ISO 527-2/1A |
| Elongation at Break | 35 % | 35 % | 50 mm/min; ISO 527-2/1A |
| Elongation at Yield | 4.0 % | 4.0 % | 50 mm/min; ISO 527-2/1A |
| Tensile Modulus | 2.60 GPa | 377 ksi | 1 mm/min; ISO 527-2/1A |
| Flexural Strength | 80.0 MPa | 11600 psi | ISO 178 |
| Flexural Modulus | 2.50 GPa | 363 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | ISO 180/1A |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| 19.0 J/cm² @Temperature -30.0 °C | 90.4 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179/1eA |
| 0.600 J/cm² @Temperature -30.0 °C | 2.86 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 3.5 @Frequency 1e+6 Hz | 3.5 @Frequency 1e+6 Hz | IEC 60250 |
| Dielectric Strength | 23.0 kV/mm | 584 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.0014 @Frequency 100 Hz | 0.0014 @Frequency 100 Hz | IEC 60250 |
| 0.022 @Frequency 1e+6 Hz | 0.022 @Frequency 1e+6 Hz | IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 110 µm/m-°C @Temperature 20.0 °C | 61.1 µin/in-°F @Temperature 68.0 °F | ISO 11359-2 |
| Melting Point | 225 °C | 437 °F | ISO 11357-1,2,3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 150 °C | 302 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ISO 75-1, -2 |
| Flammability, UL94 | HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 230 - 240 °C | 446 - 464 °F | |
| Middle Barrel Temperature | 235 - 250 °C | 455 - 482 °F | |
| Front Barrel Temperature | 240 - 260 °C | 464 - 500 °F | |
| Nozzle Temperature | 250 - 260 °C | 482 - 500 °F | |
| Melt Temperature | 235 - 260 °C | 455 - 500 °F | |
| Mold Temperature | 65.0 - 93.0 °C | 149 - 199 °F | |
| Drying Temperature | 121 °C | 250 °F | |
| Dry Time | 4 hour | 4 hour | |
| Back Pressure | 0.000 - 0.345 MPa | 0.000 - 50.0 psi | |