- 熔体流动速率 [g/10min]: 45.98
- 密度 [g/cm3]: 1.21
- 吸水率 [%]: 0.8
- 拉伸强度 [MPa]: 27.0
- 热变形温度 [℃]: 130.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.21 g/cc | 0.0437 lb/in³ | ISO 1183 |
| Water Absorption at Saturation | 0.80 % | 0.80 % | ISO 62 |
| Melt Flow | 45.98 g/10 min @Load 10.0 kg, Temperature 260 °C | 45.98 g/10 min @Load 22.0 lb, Temperature 500 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 65 | 65 | ISO 868 |
| Tensile Strength, Yield | 27.0 MPa | 3920 psi | ISO 527-1/2 |
| Elongation at Break | 10 % | 10 % | ISO 527-1/2 |
| Elongation at Yield | 3.0 % | 3.0 % | ISO 527-1/2 |
| Tensile Modulus | 1.60 GPa | 232 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179/1eU |
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 1.20 J/cm² @Temperature -30.0 °C | 5.71 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA |
| 4.50 J/cm² @Temperature 23.0 °C | 21.4 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |
| Electrical Properties | Metric | English | Comments |
| Surface Resistance | 1.00e+6 ohm | 1.00e+6 ohm | IEC 60093 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 140 µm/m-°C @Temperature 23.0 - 80.0 °C | 77.8 µin/in-°F @Temperature 73.4 - 176 °F | Longitudinal; ISO 11359, DIN 53752 |
| CTE, linear, Transverse to Flow | 140 µm/m-°C @Temperature 23.0 - 80.0 °C | 77.8 µin/in-°F @Temperature 73.4 - 176 °F | ISO 11359, DIN 53752 |
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C | 266 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ISO 75-1/-2 |
| Vicat Softening Point | 105 °C | 221 °F | Method B, 50 N; ISO 306 |
| 210 °C | 410 °F | Method A, 10 N; ISO 306 | |