- 熔体流动速率 [g/10min]: 30.8
- 密度 [g/cm3]: 1.4
- 缺口冲击强度: 10.0
- 弯曲模量 [MPa]: 6.20
- 热变形温度 [℃]: 215.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.700 g/cc | 0.0253 lb/in³ | ISO 60 |
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | 60x60x2; 270°C / MT 80°C; 600 bar; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | 60x60x2; 270°C / MT 80°C; 600 bar; ISO 294-4 |
| Melt Flow | 30.8 g/10 min @Load 2.16 kg, Temperature 270 °C | 30.8 g/10 min @Load 4.76 lb, Temperature 518 °F | ISO 1133-1 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 100 MPa | 14500 psi | 5 mm/min; ISO 527-1,-2 |
| Elongation at Break | 2.9 % | 2.9 % | 5 mm/min; ISO 527-1,-2 |
| 3.2 % | 3.2 % | 50 mm/min; ISO 527-1,-2 | |
| Tensile Modulus | 6.50 GPa | 943 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Strength | 165 MPa | 23900 psi | 2 mm/min; ISO 178-A |
| Flexural Modulus | 6.20 GPa | 899 ksi | 2 mm/min; ISO 178-A |
| Izod Impact, Notched (ISO) | <= 10.0 kJ/m² @Temperature 23.0 °C | <= 4.76 ft-lb/in² @Temperature 73.4 °F | ISO 180-1A |
| <= 10.0 kJ/m² @Temperature -30.0 °C | <= 4.76 ft-lb/in² @Temperature -22.0 °F | ISO 180-1A | |
| Izod Impact, Unnotched (ISO) | 40.0 kJ/m² @Temperature -30.0 °C | 19.0 ft-lb/in² @Temperature -22.0 °F | ISO 180-1U |
| 45.0 kJ/m² @Temperature 23.0 °C | 21.4 ft-lb/in² @Temperature 73.4 °F | ISO 180-1U | |
| Charpy Impact Unnotched | 4.00 J/cm² @Temperature -30.0 °C | 19.0 ft-lb/in² @Temperature -22.0 °F | ISO 179-1eU |
| 5.00 J/cm² @Temperature 23.0 °C | 23.8 ft-lb/in² @Temperature 73.4 °F | ISO 179-1eU | |
| Charpy Impact, Notched | <= 1.00 J/cm² @Temperature 23.0 °C | <= 4.76 ft-lb/in² @Temperature 73.4 °F | ISO 179-1eA |
| <= 1.00 J/cm² @Temperature -30.0 °C | <= 4.76 ft-lb/in² @Temperature -22.0 °F | ISO 179-1eA | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 225 °C | 437 °F | 10 °C/min; ISO 11357-1,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 185 °C | 365 °F | ISO 75-1,-2 |
| Vicat Softening Point | 170 °C | 338 °F | 50 N; 50 °C/h; ISO 306 |
| Shrinkage | 0.10 % | 0.10 % | post-shrinkage, transverse, 60x60x2; 120°C; 4 h; ISO 294-4 |
| 0.20 % | 0.20 % | post-shrinkage, 60x60x2; 120°C; 4 h; ISO 294-4 | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 270 °C | 518 °F | Injection molding; ISO 294 |
| Mold Temperature | 90.0 °C | 194 °F | Injection molding; ISO 294 |
| Dry Time | 4.00 - 8.00 hour @Temperature 120 °C | 4.00 - 8.00 hour @Temperature 248 °F | |
| Moisture Content | 0.00 - 0.020 % | 0.00 - 0.020 % | Karl Fischer test |