- 缺口冲击强度: 0.48
- 拉伸强度 [MPa]: 51.0
- 弯曲模量 [MPa]: 2.10
- 硬度: 117.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.27 g/cc | 1.27 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 117 | 117 | ASTM D785 |
| Tensile Strength at Break | 26.0 MPa | 3770 psi | ASTM D638 |
| Tensile Strength, Yield | 51.0 MPa | 7400 psi | ASTM D638 |
| Elongation at Break | 72 % | 72 % | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Strength | 72.0 MPa | 10400 psi | ASTM D790 |
| Flexural Modulus | 2.10 GPa | 305 ksi | ASTM D790 |
| Izod Impact, Notched | 0.480 J/cm @Temperature 23.0 °C | 0.899 ft-lb/in @Temperature 73.4 °F | ASTM D256 |
| 0.530 J/cm @Temperature -40.0 °C | 0.993 ft-lb/in @Temperature -40.0 °F | ASTM D256 | |
| Izod Impact, Unnotched | NB | NB | ASTM D4812 |
| NB @Temperature -40.0 °C | NB @Temperature -40.0 °F | ASTM D4812 | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 210 - 270 °C | 410 - 518 °F | Extrusion |
| 250 - 270 °C | 482 - 518 °F | Injection Molding | |
| Mold Temperature | 15.0 - 40.0 °C | 59.0 - 104 °F | |
| Drying Temperature | 70.0 °C | 158 °F | |
| Dry Time | 6 hour | 6 hour | |