Styron EMERGE™ 9100 CR Polycarbonate (PC) / Polyethylene Terephthalate (PET)

Styron EMERGE™ 9100 CR Polycarbonate (PC) / Polyethylene Terephthalate (PET) 物性表: Styron EMERGE™ 9100 CR Polycarbonate (PC) / Polyethylene Terephthalate (PET)物性表及特性介绍,Styron EMERGE™ 9100 CR Polycarbonate (PC) / Polyethylene Terephthalate (PET)注塑参数详情,如需Styron EMERGE™ 9100 CR Polycarbonate (PC) / Polyethylene Terephthalate (PET)下载, 可到相关下载区下载
  • 熔体流动速率 [g/10min]: 8.5
  • 密度 [g/cm3]: 1.23
  • 缺口冲击强度: 7.5
  • 拉伸强度 [MPa]: 50.0
  • 弯曲模量 [MPa]: 2.10
  • 硬度: 111.0
  • 热变形温度 [℃]: 117.0
 
Physical PropertiesMetricEnglishComments
Density 1.23 g/cc0.0444 lb/in³ASTM D792
Linear Mold Shrinkage, Flow 0.0060 - 0.0090 cm/cm0.0060 - 0.0090 in/inASTM D955
Linear Mold Shrinkage, Transverse 0.0050 - 0.0080 cm/cm0.0050 - 0.0080 in/inASTM D955
Melt Flow 8.5 g/10 min
@Load 5.00 kg,
Temperature 260 °C
8.5 g/10 min
@Load 11.0 lb,
Temperature 500 °F
ASTM D1238
 
Mechanical PropertiesMetricEnglishComments
Hardness, Rockwell R 111
@Thickness 3.20 mm
111
@Thickness 0.126 in
Injection Molded; ASTM D785
Tensile Strength at Break 56.2 MPa
@Thickness 3.20 mm
8150 psi
@Thickness 0.126 in
50 mm/min, Injection Molded; ASTM D638
Tensile Strength, Yield 50.0 MPa
@Thickness 3.20 mm
7250 psi
@Thickness 0.126 in
50 mm/min, Injection Molded; ASTM D638
Elongation at Break 150 %
@Thickness 3.20 mm
150 %
@Thickness 0.126 in
50 mm/min, Injection Molded; ASTM D638
Elongation at Yield 4.7 %
@Thickness 3.20 mm
4.7 %
@Thickness 0.126 in
50 mm/min, Injection Molded; ASTM D638
Tensile Modulus 2.21 GPa
@Thickness 3.20 mm
321 ksi
@Thickness 0.126 in
5 mm/min, Injection Molded; ASTM D638
Flexural Strength 77.2 MPa
@Thickness 3.20 mm
11200 psi
@Thickness 0.126 in
1.3 mm/min, Injection Molded; ASTM D790
Flexural Modulus 2.10 GPa
@Thickness 3.20 mm
305 ksi
@Thickness 0.126 in
1.3 mm/min, Injection Molded; ASTM D790
Izod Impact, Notched  7.50 J/cm
@Thickness 3.20 mm,
Temperature -30.0 °C
14.1 ft-lb/in
@Thickness 0.126 in,
Temperature -22.0 °F
Injection Molded; ASTM D256
 9.50 J/cm
@Thickness 3.20 mm,
Temperature 23.0 °C
17.8 ft-lb/in
@Thickness 0.126 in,
Temperature 73.4 °F
Injection Molded; ASTM D256
Dart Drop, Total Energy  46.3 J
@Thickness 3.20 mm,
Temperature 23.0 °C
34.1 ft-lb
@Thickness 0.126 in,
Temperature 73.4 °F
Injection Molded, Peak Energy; ASTM D3763
 55.4 J
@Thickness 3.20 mm,
Temperature -40.0 °C
40.9 ft-lb
@Thickness 0.126 in,
Temperature -40.0 °F
Injection Molded, Peak Energy; ASTM D3763
 63.3 J
@Thickness 3.20 mm,
Temperature 23.0 °C
46.7 ft-lb
@Thickness 0.126 in,
Temperature 73.4 °F
Injection Molded, Total Energy; ASTM D3763
 80.2 J
@Thickness 3.20 mm,
Temperature -40.0 °C
59.2 ft-lb
@Thickness 0.126 in,
Temperature -40.0 °F
Injection Molded, Total Energy; ASTM D3763
 
Thermal PropertiesMetricEnglishComments
Deflection Temperature at 0.46 MPa (66 psi) 117 °C243 °FUnannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 87.2 °C189 °FUnannealed; ASTM D648
Vicat Softening Point 144 °C
@Load 1.02 kg
291 °F
@Load 2.25 lb
Rate B (120°C/h); ASTM D1525
Flammability, UL94 HB
@Thickness 1.00 mm
HB
@Thickness 0.0394 in
 
Processing PropertiesMetricEnglishComments
Melt Temperature 249 - 282 °C480 - 540 °F
Mold Temperature 43.3 - 65.6 °C110 - 150 °F
Drying Temperature 121 °C250 °F
Dry Time 3.00 - 4.00 hour3.00 - 4.00 hour

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-38938.html

免责声明: 本文 Styron EMERGE™ 9100 CR Polycarbonate (PC) / Polyethylene Terephthalate (PET) 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4