- 密度 [g/cm3]: 1.3
- 吸水率 [%]: 0.13
- 缺口冲击强度: 0.98
- 拉伸强度 [MPa]: 49.0
- 断裂伸长率 [%]: 69.0
- 弯曲强度 [MPa]: 27.0
- 弯曲模量 [MPa]: 2.10
- 硬度: 106.0
- 热变形温度 [℃]: 69.0
- 透光率 [%]: 91.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ASTM D792 |
| Water Absorption | 0.13 % | 0.13 % | 24 hour immersion; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0035 cm/cm @Thickness 3.20 mm | 0.0035 in/in @Thickness 0.126 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 106 | 106 | ASTM D785 |
| Tensile Strength, Ultimate | 27.0 MPa | 3920 psi | ISO 527 |
| 30.0 MPa | 4350 psi | ASTM D638 | |
| Tensile Strength, Yield | 49.0 MPa | 7110 psi | ASTM D638 and ISO 527 |
| Elongation at Break | 110 % | 110 % | ISO 527 |
| Elongation at Yield | 4.0 % | 4.0 % | ISO 527 |
| Tensile Modulus | 2.02 GPa | 293 ksi | ISO 527 |
| Flexural Yield Strength | 69.0 MPa | 10000 psi | ISO 178 |
| Flexural Modulus | 2.10 GPa | 305 ksi | ISO 178 |
| Izod Impact, Notched | 0.980 J/cm | 1.84 ft-lb/in | ASTM D256 |
| 0.270 J/cm @Temperature -40.0 °C | 0.506 ft-lb/in @Temperature -40.0 °F | ASTM D256 | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 69.0 °C | 156 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 62.0 °C | 144 °F | ISO 75 |
| Optical Properties | Metric | English | Comments |
| Haze | 0.30 % | 0.30 % | ASTM D1003 |
| Transmission, Visible | 91 % | 91 % | Total Transmittance; ASTM D 1003 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 260 °C | 500 °F | |
| Mold Temperature | 27.0 °C | 80.6 °F | |
| Drying Temperature | 71.0 °C | 160 °F | |
| Dry Time | 5 hour | 5 hour | |