- 密度 [g/cm3]: 1.48
- 吸水率 [%]: 0.07
- 缺口冲击强度: 0.32
- 断裂伸长率 [%]: 125
- 弯曲强度 [MPa]: 82.9
- 弯曲模量 [MPa]: 6.06
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | ASTM D792 |
| Water Absorption | 0.070 % | 0.070 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0021 cm/cm | 0.0021 in/in | ATM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 82.9 MPa | 12000 psi | ASTM D638 |
| Elongation at Break | 1.29 % | 1.29 % | ASTM D638 |
| Flexural Yield Strength | 125 MPa | 18100 psi | ASTM D790 |
| Flexural Modulus | 6.06 GPa | 879 ksi | ASTM D790 |
| Compressive Yield Strength | 152 MPa | 22000 psi | ASTM D695 |
| Izod Impact, Notched | 0.320 J/cm | 0.599 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.2 @Frequency 1e+6 Hz | 3.2 @Frequency 1e+6 Hz | ASTM D150 |
| Dielectric Strength | 16.6 kV/mm | 422 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.013 @Frequency 1e+6 Hz | 0.013 @Frequency 1e+6 Hz | ASTM D150 |
| Arc Resistance | 90 sec | 90 sec | ASTM D495 |
| Comparative Tracking Index | 250 V | 250 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 206 °C | 403 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.47 mm | HB @Thickness 0.0579 in | |