- 密度 [g/cm3]: 1.73
- 吸水率 [%]: 0.05
- 缺口冲击强度: 0.68
- 断裂伸长率 [%]: 206.1
- 弯曲强度 [MPa]: 137.9
- 弯曲模量 [MPa]: 10.94
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.73 g/cc | 0.0625 lb/in³ | ASTM D792 |
| Water Absorption | 0.050 % | 0.050 % | ASTM D570 |
| Linear Mold Shrinkage | 0.00090 cm/cm | 0.00090 in/in | ATM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 137.9 MPa | 20000 psi | ASTM D638 |
| Elongation at Break | 1.65 % | 1.65 % | ASTM D638 |
| Tensile Modulus | 11.41 GPa | 1655 ksi | ASTM D638 |
| Flexural Yield Strength | 206.1 MPa | 29890 psi | ASTM D790 |
| Flexural Modulus | 10.94 GPa | 1587 ksi | ASTM D790 |
| Compressive Yield Strength | 164.7 MPa | 23890 psi | ASTM D695 |
| Izod Impact, Notched | 0.680 J/cm | 1.27 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 5.9566e+17 ohm-cm | 5.9566e+17 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.4 @Frequency 1e+6 Hz | 3.4 @Frequency 1e+6 Hz | ASTM D150 |
| Dielectric Strength | 16.1 kV/mm | 409 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.011 @Frequency 1e+6 Hz | 0.011 @Frequency 1e+6 Hz | ASTM D150 |
| Arc Resistance | 40 sec | 40 sec | ASTM D495 |
| Comparative Tracking Index | 200 V | 200 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.47 mm | V-0 @Thickness 0.0579 in | |