SABIC Innovative Plastics Xenoy X3515 PC+POLYESTER (Asia Pacific)

SABIC Innovative Plastics Xenoy X3515 PC+POLYESTER (Asia Pacific) 物性表: SABIC Innovative Plastics Xenoy X3515 PC+POLYESTER (Asia Pacific)物性表及特性介绍,SABIC Innovative Plastics Xenoy X3515 PC+POLYESTER (Asia Pacific)注塑参数详情,如需SABIC Innovative Plastics Xenoy X3515 PC+POLYESTER (Asia Pacific)下载, 可到相关下载区下载
  • 熔体流动速率 [g/10min]: 4.0
  • 密度 [g/cm3]: 1.3
  • 吸水率 [%]: 0.5
  • 缺口冲击强度: 4.27
  • 拉伸强度 [MPa]: 47.0
  • 断裂伸长率 [%]: 71.0
  • 弯曲模量 [MPa]: 1.86
  • 热变形温度 [℃]: 114.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.30 g/cc1.30 g/ccASTM D 792
Density 1.30 g/cc0.0470 lb/in³ISO 1183
Moisture Absorption at Equilibrium 0.15 %0.15 %23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.50 %
@Temperature 23.0 °C		0.50 %
@Temperature 73.4 °F		ISO 62
Linear Mold Shrinkage, Flow 0.0080 - 0.010 cm/cm
@Thickness 3.20 mm		0.0080 - 0.010 in/in
@Thickness 0.126 in		SABIC Method
Linear Mold Shrinkage, Transverse 0.0080 - 0.010 cm/cm
@Thickness 3.20 mm		0.0080 - 0.010 in/in
@Thickness 0.126 in		SABIC Method
Melt Flow  4.0 g/10 min
@Load 2.16 kg,
Temperature 250 °C		4.0 g/10 min
@Load 4.76 lb,
Temperature 482 °F		ISO 1133
 4.0 g/10 min
@Load 2.16 kg,
Temperature 250 °C		4.0 g/10 min
@Load 4.76 lb,
Temperature 482 °F		[cm^3/10 min] Melt Volume Rate; ISO 1133
 4.8 g/10 min
@Load 2.16 kg,
Temperature 250 °C		4.8 g/10 min
@Load 4.76 lb,
Temperature 482 °F		ASTM D 1238
 7.0 g/10 min
@Load 2.16 kg,
Temperature 265 °C		7.0 g/10 min
@Load 4.76 lb,
Temperature 509 °F		[cm^3/10 min] Melt Volume Rate; ISO 1133
 8.0 g/10 min
@Load 2.16 kg,
Temperature 265 °C		8.0 g/10 min
@Load 4.76 lb,
Temperature 509 °F		ASTM D 1238
 13 g/10 min
@Load 5.00 kg,
Temperature 250 °C		13 g/10 min
@Load 11.0 lb,
Temperature 482 °F		[cm^3/10 min] Melt Volume Rate; ISO 1133
 15 g/10 min
@Load 5.00 kg,
Temperature 250 °C		15 g/10 min
@Load 11.0 lb,
Temperature 482 °F		ISO 1133
 15.1 g/10 min
@Load 5.00 kg,
Temperature 250 °C		15.1 g/10 min
@Load 11.0 lb,
Temperature 482 °F		ASTM D 1238
 23 g/10 min
@Load 5.00 kg,
Temperature 265 °C		23 g/10 min
@Load 11.0 lb,
Temperature 509 °F		[cm^3/10 min] Melt Volume Rate; ISO 1133
 26.7 g/10 min
@Load 5.00 kg,
Temperature 266 °C		26.7 g/10 min
@Load 11.0 lb,
Temperature 511 °F		ASTM D 1238
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break 40.0 MPa5800 psi50 mm/min; ISO 527
 42.0 MPa6090 psiType I, 50 mm/min; ASTM D 638
Tensile Strength, Yield 47.0 MPa6820 psi50 mm/min; ISO 527
 52.0 MPa7540 psiType I, 50 mm/min; ASTM D 638
Elongation at Break 44 %44 %Type I, 50 mm/min; ASTM D 638
 58 %58 %50 mm/min; ISO 527
Elongation at Yield 4.1 %4.1 %50 mm/min; ISO 527
 4.3 %4.3 %Type I, 50 mm/min; ASTM D 638
Tensile Modulus 1.96 GPa284 ksi1 mm/min; ISO 527
 2.15 GPa312 ksi5 mm/min; ASTM D 638
Flexural Yield Strength 71.0 MPa10300 psi2 mm/min; ISO 178
 72.0 MPa10400 psi1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 1.86 GPa270 ksi1.3 mm/min, 50 mm span; ASTM D 790
 1.89 GPa274 ksi2 mm/min; ISO 178
Izod Impact, Notched  4.27 J/cm
@Temperature -40.0 °C		8.00 ft-lb/in
@Temperature -40.0 °F		ASTM D 256
 4.50 J/cm
@Temperature -30.0 °C		8.43 ft-lb/in
@Temperature -22.0 °F		ASTM D 256
 6.94 J/cm
@Temperature -20.0 °C		13.0 ft-lb/in
@Temperature -4.00 °F		ASTM D 256
 7.47 J/cm
@Temperature 23.0 °C		14.0 ft-lb/in
@Temperature 73.4 °F		ASTM D 256
Izod Impact, Notched (ISO)  40.0 kJ/m²
@Temperature -30.0 °C		19.0 ft-lb/in²
@Temperature -22.0 °F		80*10*4; ISO 180/1A
 43.0 kJ/m²
@Temperature -10.0 °C		20.5 ft-lb/in²
@Temperature 14.0 °F		80*10*4; ISO 180/1A
 47.0 kJ/m²
@Temperature 0.000 °C		22.4 ft-lb/in²
@Temperature 32.0 °F		80*10*4; ISO 180/1A
 53.0 kJ/m²
@Temperature 23.0 °C		25.2 ft-lb/in²
@Temperature 73.4 °F		80*10*4; ISO 180/1A
Charpy Impact, Notched 5.30 J/cm²
@Temperature 23.0 °C		25.2 ft-lb/in²
@Temperature 73.4 °F		V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
Impact Test  56.0 J
@Temperature -20.0 °C		41.3 ft-lb
@Temperature -4.00 °F		Instrumented Impact, Energy @ peak; ASTM D 3763
 62.0 J
@Temperature 23.0 °C		45.7 ft-lb
@Temperature 73.4 °F		Instrumented Impact Total Energy; ASTM D 3763
 70.0 J
@Temperature -30.0 °C		51.6 ft-lb
@Temperature -22.0 °F		Instrumented Impact Energy @ peak; ASTM D 3763
 74.0 J
@Temperature -40.0 °C		54.6 ft-lb
@Temperature -40.0 °F		Instrumented Impact Energy @ peak; ASTM D 3763
 
Electrical PropertiesMetricEnglishComments
Arc Resistance 120 - 180 sec120 - 180 secTungsten, PLC code 5; ASTM D 495
Comparative Tracking Index >= 600 V>= 600 VPLC code 0; UL 746A
Hot Wire Ignition, HWI 30 - 60 sec30 - 60 secPLC code 2; UL 746A
High Amp Arc Ignition, HAI >= 120 arcs>= 120 arcssurface, PLC code 0; UL 746A
High Voltage Arc-Tracking Rate, HVTR 25.4 - 80.0 mm/min1.00 - 3.15 in/minPLC code 2; UL 746A
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow  98.0 µm/m-°C
@Temperature -40.0 - 40.0 °C		54.4 µin/in-°F
@Temperature -40.0 - 104 °F		ASTM E 831
 98.0 µm/m-°C
@Temperature -40.0 - 40.0 °C		54.4 µin/in-°F
@Temperature -40.0 - 104 °F		ISO 11359-2
CTE, linear, Transverse to Flow  100 µm/m-°C
@Temperature -40.0 - 40.0 °C		55.6 µin/in-°F
@Temperature -40.0 - 104 °F		ASTM E 831
 100 µm/m-°C
@Temperature -40.0 - 40.0 °C		55.6 µin/in-°F
@Temperature -40.0 - 104 °F		ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 114 °C237 °FFlatw 80*10*4 sp=64mm; ISO 75/Bf
 110 °C
@Thickness 3.20 mm		230 °F
@Thickness 0.126 in		unannealed; ASTM D 648
 123 °C
@Thickness 6.40 mm		253 °F
@Thickness 0.252 in		unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 88.0 °C190 °FFlatw 80*10*4 sp=64mm; ISO 75/Af
 74.0 °C
@Thickness 3.20 mm		165 °F
@Thickness 0.126 in		unannealed; ASTM D 648
 95.0 °C
@Thickness 6.40 mm		203 °F
@Thickness 0.252 in		unannealed; ASTM D 648
Vicat Softening Point 120 °C248 °FRate B/50; ASTM D 1525
 120 °C248 °FRate B/50; ISO 306
 122 °C252 °FRate B/120; ISO 306
UL RTI, Electrical 75.0 °C167 °FUL 746B
UL RTI, Mechanical with Impact 75.0 °C167 °FUL 746B
UL RTI, Mechanical without Impact 75.0 °C167 °FUL 746B
Flammability, UL94  V-0
@Thickness 1.47 mm		V-0
@Thickness 0.0579 in		UL 94 by SABIC-IP
 5VA
@Thickness 2.99 mm		5VA
@Thickness 0.118 in		UL 94 by SABIC-IP
Oxygen Index 28 %28 %LOI; ISO 4589

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-39496.html

免责声明: 本文 SABIC Innovative Plastics Xenoy X3515 PC+POLYESTER (Asia Pacific) 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络