- 吸水率 [%]: 0.07
- 缺口冲击强度: 0.42
- 拉伸强度 [MPa]: 132.0
- 弯曲模量 [MPa]: 10.14
- 热变形温度 [℃]: 205.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.80 g/cc | 1.80 g/cc | ASTM D 792 |
| Water Absorption | 0.070 % @Time 86400 sec | 0.070 % @Time 24.0 hour | ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Thickness 3.20 mm | 0.0030 - 0.0050 in/in @Thickness 0.126 in | SABIC Method |
| 0.0080 - 0.013 cm/cm @Thickness 6.40 mm | 0.0080 - 0.013 in/in @Thickness 0.252 in | SABIC Method | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 132 MPa | 19100 psi | SABIC - Japan Method |
| Elongation at Break | 10 % | 10 % | SABIC - Japan Method |
| Flexural Strength | 162 MPa | 23500 psi | ASTM D 790 |
| Flexural Modulus | 10.14 GPa | 1471 ksi | ASTM D 790 |
| Izod Impact, Notched | 0.420 J/cm @Temperature 23.0 °C | 0.787 ft-lb/in @Temperature 73.4 °F | ASTM D 256 |
| Izod Impact, Unnotched | 4.31 J/cm @Temperature 23.0 °C | 8.07 ft-lb/in @Temperature 73.4 °F | ASTM D 4812 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 30.0 - 80.0 µm/m-°C @Temperature -30.0 - 30.0 °C | 16.7 - 44.4 µin/in-°F @Temperature -22.0 - 86.0 °F | TMA |
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C @Thickness 3.20 mm | 401 °F @Thickness 0.126 in | unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 218 °C @Thickness 3.20 mm | 424 °F @Thickness 0.126 in | unannealed; ASTM D 648 |