- 熔体流动速率 [g/10min]: 9.0
- 密度 [g/cm3]: 1.51
- 吸水率 [%]: 0.5
- 缺口冲击强度: 0.6
- 拉伸强度 [MPa]: 100.0
- 断裂伸长率 [%]: 140
- 弯曲模量 [MPa]: 7.00
- 硬度: 110.0
- 热变形温度 [℃]: 215.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.51 g/cc | 1.51 g/cc | ASTM D 792 | ||
| Density | 1.51 g/cc | 0.0546 lb/in³ | ISO 1183 | ||
| Moisture Absorption at Equilibrium | 0.15 % | 0.15 % | 23°C / 50% RH; ISO 62 | ||
| Water Absorption at Saturation | 0.50 % @Temperature 23.0 °C | 0.50 % @Temperature 73.4 °F | ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0070 cm/cm | 0.0030 - 0.0070 in/in | on tensile bar; SABIC Method | ||
| 0.0030 - 0.0070 cm/cm @Thickness 3.20 mm | 0.0030 - 0.0070 in/in @Thickness 0.126 in | SABIC Method | |||
| Melt Flow | 9.0 g/10 min @Load 1.20 kg, Temperature 265 °C | 9.0 g/10 min @Load 2.65 lb, Temperature 509 °F | [cm^3/10 min] Melt Volume Rate; ISO 1133 | ||
| 13 g/10 min @Load 1.20 kg, Temperature 266 °C | 13 g/10 min @Load 2.65 lb, Temperature 511 °F | ASTM D 1238 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 110 | 110 | ISO 2039-2 | ||
| Hardness, H358/30 | 115 MPa | 16700 psi | ISO 2039-1 | ||
| Tensile Strength at Break | 100 MPa | 14500 psi | Type I, 5 mm/min; ASTM D 638 | ||
| 105 MPa | 15200 psi | 5 mm/min; ISO 527 | |||
| Tensile Strength, Yield | 100 MPa | 14500 psi | Type I, 5 mm/min; ASTM D 638 | ||
| 105 MPa | 15200 psi | 5 mm/min; ISO 527 | |||
| Elongation at Break | 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D 638 | ||
| 2.0 % | 2.0 % | 5 mm/min; ISO 527 | |||
| Elongation at Yield | 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D 638 | ||
| 2.0 % | 2.0 % | 5 mm/min; ISO 527 | |||
| Tensile Modulus | 8.20 GPa | 1190 ksi | 5 mm/min; ASTM D 638 | ||
| 8.40 GPa | 1220 ksi | 1 mm/min; ISO 527 | |||
| Flexural Strength | 145 MPa | 21000 psi | break, 2 mm/min; ISO 178 | ||
| Flexural Yield Strength | 140 MPa | 20300 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | ||
| Flexural Modulus | 7.00 GPa | 1020 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | ||
| 7.20 GPa | 1040 ksi | 2 mm/min; ISO 178 | |||
| Izod Impact, Notched | 0.600 J/cm @Temperature -30.0 °C | 1.12 ft-lb/in @Temperature -22.0 °F | ASTM D 256 | ||
| 0.800 J/cm @Temperature 23.0 °C | 1.50 ft-lb/in @Temperature 73.4 °F | ASTM D 256 | |||
| Izod Impact, Unnotched | 6.00 J/cm @Temperature -30.0 °C | 11.2 ft-lb/in @Temperature -22.0 °F | ASTM D 4812 | ||
| 6.50 J/cm @Temperature 23.0 °C | 12.2 ft-lb/in @Temperature 73.4 °F | ASTM D 4812 | |||
| Izod Impact, Notched (ISO) | 6.00 kJ/m² @Temperature -30.0 °C | 2.86 ft-lb/in² @Temperature -22.0 °F | 80*10*4; ISO 180/1A | ||
| 10.0 kJ/m² @Temperature 23.0 °C | 4.76 ft-lb/in² @Temperature 73.4 °F | 80*10*4; ISO 180/1A | |||
| Izod Impact, Unnotched (ISO) | 40.0 kJ/m² @Temperature 23.0 °C | 19.0 ft-lb/in² @Temperature 73.4 °F | 80*10*4; ISO 180/1U | ||
| 40.0 kJ/m² @Temperature -30.0 °C | 19.0 ft-lb/in² @Temperature -22.0 °F | 80*10*4; ISO 180/1U | |||
| Charpy Impact Unnotched | 3.50 J/cm² @Temperature -30.0 °C | 16.7 ft-lb/in² @Temperature -22.0 °F | Edgew 80*10*4 sp=62mm; ISO 179/1eU | ||
| 4.00 J/cm² @Temperature 23.0 °C | 19.0 ft-lb/in² @Temperature 73.4 °F | Edgew 80*10*4 sp=62mm; ISO 179/1eU | |||
| Charpy Impact, Notched | 0.700 J/cm² @Temperature -30.0 °C | 3.33 ft-lb/in² @Temperature -22.0 °F | V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA | ||
| 1.00 J/cm² @Temperature 23.0 °C | 4.76 ft-lb/in² @Temperature 73.4 °F | V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA | |||
| Impact Test | 7.00 J @Temperature 23.0 °C | 5.16 ft-lb @Temperature 73.4 °F | Instrumented Impact Total Energy; ASTM D 3763 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | IEC 60093 | ||
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 | ||
| Dielectric Constant | 4.0 @Frequency 1.00e+6 Hz | 4.0 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 4.2 @Frequency 50.0 - 60.0 Hz | 4.2 @Frequency 50.0 - 60.0 Hz | IEC 60250 | |||
| Dielectric Strength | 17.0 kV/mm @Thickness 3.20 mm | 432 kV/in @Thickness 0.126 in | in oil; IEC 60243-1 | ||
| 20.0 kV/mm @Thickness 1.60 mm | 508 kV/in @Thickness 0.0630 in | in oil; IEC 60243-1 | |||
| Dissipation Factor | 0.0020 @Frequency 50.0 - 60.0 Hz | 0.0020 @Frequency 50.0 - 60.0 Hz | IEC 60250 | ||
| 0.020 @Frequency 1.00e+6 Hz | 0.020 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Comparative Tracking Index | 300 V | 300 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 23.0 µm/m-°C @Temperature 23.0 - 80.0 °C | 12.8 µin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 | ||
| 25.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 13.9 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 | |||
| CTE, linear, Transverse to Flow | 100 µm/m-°C @Temperature -40.0 - 40.0 °C | 55.6 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 | ||
| 130 µm/m-°C @Temperature 23.0 - 80.0 °C | 72.2 µin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 | |||
| Thermal Conductivity | 0.190 W/m-K | 1.32 BTU-in/hr-ft²-°F | ISO 8302 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 180 °C | 356 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af | ||
| 165 °C @Thickness 3.20 mm | 329 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |||
| Vicat Softening Point | 180 °C | 356 °F | Rate B/50; ASTM D 1525 | ||
| 180 °C | 356 °F | Rate B/50; ISO 306 | |||
| 180 °C | 356 °F | Rate B/120; ISO 306 | |||
| 215 °C | 419 °F | Rate A/50; ISO 306 | |||
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | UL 94 | ||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | 2nd value; UL 94 | |||
| Glow Wire Test | 750 °C @Thickness 3.20 mm | 1380 °F @Thickness 0.126 in | Glow Wire Flammability Index; IEC 60695-2-12 | ||
| Descriptive Properties | |||||
| Ball Pressure Test, 125°C +/- 2°C | PASSES | IEC 60695-10-2 | |||