SABIC Innovative Plastics XYLEX X8303 PC+POLYESTER (Europe-Africa-Middle East)

SABIC Innovative Plastics XYLEX X8303 PC+POLYESTER (Europe-Africa-Middle East) 物性表: SABIC Innovative Plastics XYLEX X8303 PC+POLYESTER (Europe-Africa-Middle East)物性表及特性介绍,SABIC Innovative Plastics XYLEX X8303 PC+POLYESTER (Europe-Africa-Middle East)注塑参数详情,如需SABIC Innovative Plastics XYLEX X8303 PC+POLYESTER (Europe-Africa-Middle East)下载, 可到相关下载区下载
  • 熔体流动速率 [g/10min]: 30.0
  • 密度 [g/cm3]: 1.2
  • 吸水率 [%]: 0.5
  • 缺口冲击强度: 10.0
  • 拉伸强度 [MPa]: 46.0
  • 断裂伸长率 [%]: 72.0
  • 弯曲模量 [MPa]: 1.62
  • 热变形温度 [℃]: 92.0
  • 透光率 [%]: 88.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.20 g/cc1.20 g/ccASTM D792
Density 1.20 g/cc0.0434 lb/in³ISO 1183
Moisture Absorption 0.200 %0.200 %23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.50 %0.50 %ISO 62
Linear Mold Shrinkage, Flow 0.0040 - 0.0080 cm/cm
@Thickness 3.20 mm
0.0040 - 0.0080 in/in
@Thickness 0.126 in
SABIC Method
Melt Flow 30 g/10 min
@Load 2.16 kg,
Temperature 265 °C
30 g/10 min
@Load 4.76 lb,
Temperature 509 °F
ASTM D1238
Melt Index of Compound 27 g/10 min
@Load 2.16 kg,
Temperature 265 °C
27 g/10 min
@Load 4.76 lb,
Temperature 509 °F
MVR [cm^3/10 min]; ISO 1133
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break 43.0 MPa6240 psi50 mm/min; ISO 527
 44.0 MPa6380 psiType I, 50 mm/min; ASTM D638
Tensile Strength, Yield 46.0 MPa6670 psiType I, 50 mm/min; ASTM D638
 48.0 MPa6960 psi50 mm/min; ISO 527
Elongation at Break 140 %140 %Type I, 50 mm/min; ASTM D638
 140 %140 %50 mm/min; ISO 527
Elongation at Yield 5.0 %5.0 %Type I, 50 mm/min; ASTM D638
 6.0 %6.0 %50 mm/min; ISO 527
Tensile Modulus 1.68 GPa244 ksi5 mm/min; ASTM D638
 1.69 GPa245 ksi1 mm/min; ISO 527
Flexural Strength 72.0 MPa10400 psibreak, 2 mm/min; ISO 178
Flexural Yield Strength 72.0 MPa10400 psi1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 1.62 GPa235 ksi1.3 mm/min, 50 mm span; ASTM D790
 1.72 GPa249 ksi2 mm/min; ISO 178
Izod Impact, Notched 10.0 J/cm18.7 ft-lb/inASTM D256
 1.00 J/cm
@Temperature -30.0 °C
1.87 ft-lb/in
@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 20.0 kJ/m²9.52 ft-lb/in²80*10*4; ISO 180/1A
 9.00 kJ/m²
@Temperature -30.0 °C
4.28 ft-lb/in²
@Temperature -22.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 1.40 J/cm²6.66 ft-lb/in²Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 65.0 J
@Temperature 23.0 °C
47.9 ft-lb
@Temperature 73.4 °F
ASTM D3763
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow  90.0 µm/m-°C
@Temperature -40.0 - 40.0 °C
50.0 µin/in-°F
@Temperature -40.0 - 104 °F
ASTM E 831
 92.0 µm/m-°C
@Temperature 23.0 - 60.0 °C
51.1 µin/in-°F
@Temperature 73.4 - 140 °F
ISO 11359-2
CTE, linear, Transverse to Flow  90.0 µm/m-°C
@Temperature -40.0 - 40.0 °C
50.0 µin/in-°F
@Temperature -40.0 - 104 °F
ASTM E 831
 98.0 µm/m-°C
@Temperature 23.0 - 60.0 °C
54.4 µin/in-°F
@Temperature 73.4 - 140 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 92.0 °C
@Thickness 3.20 mm
198 °F
@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 90.0 °C194 °FFlatw 80*10*4 sp=64mm; ISO 75/Af
 80.0 °C
@Thickness 3.20 mm
176 °F
@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 98.0 °C208 °FRate B/50; ASTM D1525
 100 °C212 °FRate B/50; ISO 306
 100 °C212 °FRate B/120; ISO 306
 
Optical PropertiesMetricEnglishComments
Haze 2.0 %
@Thickness 2.54 mm
2.0 %
@Thickness 0.100 in
ASTM D1003
Transmission, Visible 88 %88 %2.54 mm; ASTM D1003

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-39489.html

免责声明: 本文 SABIC Innovative Plastics XYLEX X8303 PC+POLYESTER (Europe-Africa-Middle East) 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4