- 熔体流动速率 [g/10min]: 12.0
- 密度 [g/cm3]: 1.45
- 吸水率 [%]: 0.35
- 缺口冲击强度: 5.0
- 拉伸强度 [MPa]: 100.0
- 断裂伸长率 [%]: 160
- 弯曲模量 [MPa]: 5.80
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.12 % | 0.12 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.35 % @Temperature 23.0 °C | 0.35 % @Temperature 73.4 °F | ISO 62 |
| Melt Flow | 12 g/10 min @Load 1.20 kg, Temperature 265 °C | 12 g/10 min @Load 2.65 lb, Temperature 509 °F | [cm^3/10 min] Melt Volume Rate; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 100 MPa | 14500 psi | 5 mm/min; ISO 527 |
| Tensile Strength, Yield | 100 MPa | 14500 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.2 % | 2.2 % | 5 mm/min; ISO 527 |
| Elongation at Yield | 2.2 % | 2.2 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 6.20 GPa | 899 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 160 MPa | 23200 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 5.80 GPa | 841 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature 23.0 °C | 2.38 ft-lb/in² @Temperature 73.4 °F | 80*10*4; ISO 180/1A |
| 5.00 kJ/m² @Temperature -30.0 °C | 2.38 ft-lb/in² @Temperature -22.0 °F | 80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 0.500 J/cm² @Temperature 23.0 °C | 2.38 ft-lb/in² @Temperature 73.4 °F | V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 35.0 µm/m-°C @Temperature 23.0 - 80.0 °C | 19.4 µin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 100 µm/m-°C @Temperature 23.0 - 80.0 °C | 55.6 µin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Vicat Softening Point | 230 °C | 446 °F | Rate B/50; ISO 306 |
| 235 °C | 455 °F | Rate B/120; ISO 306 | |