- 熔体流动速率 [g/10min]: 10.0
- 密度 [g/cm3]: 1.17
- 吸水率 [%]: 0.01
- 缺口冲击强度: 0.81
- 拉伸强度 [MPa]: 61.0
- 断裂伸长率 [%]: 86.0
- 弯曲模量 [MPa]: 2.15
- 热变形温度 [℃]: 118.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D 792 |
| Density | 1.17 g/cc | 0.0423 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.010 % | 0.010 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.010 % @Temperature 23.0 °C | 0.010 % @Temperature 73.4 °F | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm | 0.0050 - 0.0070 in/in @Thickness 0.126 in | SABIC Method |
| Melt Flow | 10 g/10 min @Load 2.16 kg, Temperature 265 °C | 10 g/10 min @Load 4.76 lb, Temperature 509 °F | [cm^3/10 min] Melt Volume Rate; ISO 1133 |
| 11 g/10 min @Load 2.16 kg, Temperature 265 °C | 11 g/10 min @Load 4.76 lb, Temperature 509 °F | ASTM D 1238 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 60.0 MPa | 8700 psi | 50 mm/min; ISO 527 |
| 63.0 MPa | 9140 psi | Type I, 50 mm/min; ASTM D 638 | |
| Tensile Strength, Yield | 61.0 MPa | 8850 psi | Type I, 50 mm/min; ASTM D 638 |
| 61.0 MPa | 8850 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 110 % | 110 % | Type I, 50 mm/min; ASTM D 638 |
| 125 % | 125 % | 50 mm/min; ISO 527 | |
| Elongation at Yield | 6.0 % | 6.0 % | Type I, 50 mm/min; ASTM D 638 |
| 6.0 % | 6.0 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 2.13 GPa | 309 ksi | 50 mm/min; ASTM D 638 |
| 2.30 GPa | 334 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 89.0 MPa | 12900 psi | break, 2 mm/min; ISO 178 |
| Flexural Yield Strength | 86.0 MPa | 12500 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 2.15 GPa | 312 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 2.21 GPa | 321 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.810 J/cm @Temperature -30.0 °C | 1.52 ft-lb/in @Temperature -22.0 °F | ASTM D 256 |
| 0.880 J/cm @Temperature 23.0 °C | 1.65 ft-lb/in @Temperature 73.4 °F | ASTM D 256 | |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² @Temperature -30.0 °C | 2.86 ft-lb/in² @Temperature -22.0 °F | 80*10*4; ISO 180/1A |
| 7.00 kJ/m² @Temperature 23.0 °C | 3.33 ft-lb/in² @Temperature 73.4 °F | 80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 0.600 J/cm² @Temperature 23.0 °C | 2.86 ft-lb/in² @Temperature 73.4 °F | V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Impact Test | 67.0 J @Temperature 23.0 °C | 49.4 ft-lb @Temperature 73.4 °F | Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 69.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 38.3 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 71.0 µm/m-°C @Temperature 23.0 - 60.0 °C | 39.4 µin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 38.9 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 72.0 µm/m-°C @Temperature 23.0 - 60.0 °C | 40.0 µin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C @Thickness 3.20 mm | 244 °F @Thickness 0.126 in | unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 113 °C | 235 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 105 °C @Thickness 3.20 mm | 221 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |
| Vicat Softening Point | 122 °C | 252 °F | Rate B/50; ISO 306 |
| 123 °C | 253 °F | Rate B/50; ASTM D 1525 | |
| 124 °C | 255 °F | Rate B/120; ISO 306 | |