Celanese THERMX CG023 PCT, 20% Glass Reinforced

Celanese THERMX CG023 PCT, 20% Glass Reinforced 物性表: Celanese THERMX CG023 PCT, 20% Glass Reinforced物性表及特性介绍,Celanese THERMX CG023 PCT, 20% Glass Reinforced注塑参数详情,如需Celanese THERMX CG023 PCT, 20% Glass Reinforced下载, 可到相关下载区下载
  • 熔体流动速率 [g/10min]: 30.0
  • 密度 [g/cm3]: 1.38
  • 缺口冲击强度: 6.0
  • 弯曲模量 [MPa]: 5.80
 
Physical PropertiesMetricEnglishComments
Density 1.38 g/cc0.0499 lb/in³ISO 1183
Density of Compound 1.14 g/cc0.0412 lb/in³melt; Internal
Viscosity Test 85.0 cm³/g85.0 cm³/gISO 307, 1157, 1628
Linear Mold Shrinkage, Flow 0.00300 cm/cm0.00300 in/inISO 294-4
Linear Mold Shrinkage, Transverse 0.00800 cm/cm0.00800 in/inISO 294-4
Melt Flow 30.0 g/10 min
@Load 2.16 kg,
Temperature 300 °C
30.0 g/10 min
@Load 4.76 lb,
Temperature 572 °F
(MVR) cm³/10min; ISO 1133
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break 100 MPa14500 psi5mm/min; ISO 527-2/1A
Elongation at Break 2.30 %2.30 %5mm/min; ISO 527-2/1A
Tensile Modulus 6.40 GPa928 ksi1mm/min; ISO 527-2/1A
Flexural Strength 155 MPa22500 psiISO 178
Flexural Modulus 5.80 GPa841 ksiISO 178
Izod Impact, Notched (ISO) 6.00 kJ/m²2.86 ft-lb/in²ISO 180/1A
Charpy Impact Unnotched 3.50 J/cm²16.7 ft-lb/in²ISO 179/1eU
 3.00 J/cm²
@Temperature -30.0 °C
14.3 ft-lb/in²
@Temperature -22.0 °F
ISO 179/1eU
Charpy Impact, Notched 0.700 J/cm²3.33 ft-lb/in²ISO 179/1eA
 0.700 J/cm²
@Temperature -30.0 °C
3.33 ft-lb/in²
@Temperature -22.0 °F
ISO 179/1eA
Tensile Creep Modulus, 1 hour 6000 MPa870000 psiISO 899-1
Tensile Creep Modulus, 1000 hours 4600 MPa667000 psiISO 899-1
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity 1.00e+15 ohm-cm1.00e+15 ohm-cmIEC 60093
Surface Resistance >= 1.00e+15 ohm>= 1.00e+15 ohmIEC 60093
Dielectric Strength 41.0 kV/mm1040 kV/inIEC 60243-1
 
Thermal PropertiesMetricEnglishComments
CTE, linear 30.0 µm/m-°C16.7 µin/in-°FISO 11359-2
CTE, linear, Transverse to Flow 80.0 µm/m-°C44.4 µin/in-°FISO 11359-2
Specific Heat Capacity 1.47 J/g-°C0.351 BTU/lb-°FInternal
Thermal Conductivity 0.200 W/m-K1.39 BTU-in/hr-ft²-°FInternal
Melting Point 285 °C545 °F10°C/min; ISO 11357-1,-2,-3
Transformation Temperature, Tg 105 °C221 °F10°C/min; ISO 11357-1,-2,-3
Deflection Temperature at 1.8 MPa (264 psi) 253 °C487 °FISO 75-1, -2
Flammability, UL94 HB
@Thickness 1.60 mm
HB
@Thickness 0.0630 in
UL94
 
Processing PropertiesMetricEnglishComments
Processing Temperature 80.0 - 120 °C176 - 248 °FCavity temperature
 230 °C446 °FEjection temperature; Internal
Melt Temperature 300 °C572 °FOptimum
 295 - 310 °C563 - 590 °F
 295 - 310 °C563 - 590 °F
Mold Temperature 100 °C212 °FOptimum
 80.0 - 120 °C176 - 248 °F
Drying Temperature >= 95.0 °C>= 203 °F
Dry Time 4.00 - 6.00 hour4.00 - 6.00 hour

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-39688.html

免责声明: 本文 Celanese THERMX CG023 PCT, 20% Glass Reinforced 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4