- 密度 [g/cm3]: 1.2
- 吸水率 [%]: 0.13
- 拉伸强度 [MPa]: 56.0
- 断裂伸长率 [%]: 81.0
- 弯曲强度 [MPa]: 56.0
- 弯曲模量 [MPa]: 2.10
- 硬度: 117.0
- 热变形温度 [℃]: 103.0
- 透光率 [%]: 77.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ASTM D792 and ISO 1183 |
| Water Absorption | 0.13 % | 0.13 % | 24 hour immersion; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm @Thickness 3.20 mm | 0.0060 in/in @Thickness 0.126 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 117 | 117 | ASTM D785 |
| Tensile Strength, Ultimate | 56.0 MPa | 8120 psi | ISO 527 |
| Tensile Strength, Yield | 56.0 MPa | 8120 psi | ISO 527 |
| Elongation at Break | 130 % | 130 % | ISO 527 |
| Elongation at Yield | 5.4 % | 5.4 % | ISO 527 |
| Flexural Yield Strength | 81.0 MPa | 11700 psi | ISO 178 |
| Flexural Modulus | 2.10 GPa | 305 ksi | ISO 178 |
| Izod Impact, Notched | NB | NB | ASTM D256 |
| 0.750 J/cm @Temperature -40.0 °C | 1.41 ft-lb/in @Temperature -40.0 °F | ASTM D256 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | ASTM D257 |
| Dielectric Constant | 2.1 @Frequency 1e+6 Hz | 2.1 @Frequency 1e+6 Hz | ASTM D 150 |
| 2.3 @Frequency 1000 Hz | 2.3 @Frequency 1000 Hz | ASTM D150 | |
| Dielectric Strength | 17.3 kV/mm | 439 kV/in | Short Time, 500 V/sec rate-of-rise; ASTM D 149 |
| Dissipation Factor | 0.0020 @Frequency 1000 Hz | 0.0020 @Frequency 1000 Hz | ASTM D150 |
| 0.0080 @Frequency 1e+6 Hz | 0.0080 @Frequency 1e+6 Hz | ASTM D150 | |
| Comparative Tracking Index | >= 600 V | >= 600 V | ASTM D3638 |
| High Voltage Arc-Tracking Rate, HVTR | 38.0 mm/min | 1.50 in/min | UL 746A |
| Thermal Properties | Metric | English | Comments |
| Specific Heat Capacity | 1.38 J/g-°C @Temperature 60.0 °C | 0.330 BTU/lb-°F @Temperature 140 °F | |
| 2.18 J/g-°C @Temperature 240 °C | 0.521 BTU/lb-°F @Temperature 464 °F | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 103 °C | 217 °F | ASTM D648 and ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | ASTM D648 and ISO 75 |
| Vicat Softening Point | 110 °C | 230 °F | 5 kg load; ISO 306 |
| 118 °C | 244 °F | 1 kg load; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| V-2 @Thickness 3.20 mm | V-2 @Thickness 0.126 in | natural and white | |
| V-2 @Thickness 1.60 mm | V-2 @Thickness 0.0630 in | natural and white | |
| Optical Properties | Metric | English | Comments |
| Haze | 3.6 % | 3.6 % | ASTM D1003 |
| Transmission, Visible | 77 % | 77 % | Regular transmittance per ASTM D 1003 |
| 81 % | 81 % | Total Transmittance; ASTM D 1003 | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 280 °C | 536 °F | |
| Mold Temperature | 47.5 °C | 118 °F | |
| Drying Temperature | 95.0 °C | 203 °F | |
| Dry Time | 6 hour | 6 hour | |