Celanese Thermx® CG907 PCT, 30% Glass Reinforced 物性表: Celanese Thermx® CG907 PCT, 30% Glass Reinforced物性表及特性介绍,Celanese Thermx® CG907 PCT, 30% Glass Reinforced注塑参数详情,如需Celanese Thermx® CG907 PCT, 30% Glass Reinforced下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.62
  • 缺口冲击强度: 6.0
  • 弯曲模量 [MPa]: 10.0
 
Physical PropertiesMetricEnglishComments
Density 1.62 g/cc0.0585 lb/in³ISO 1183
Linear Mold Shrinkage, Flow 0.0025 cm/cm0.0025 in/inISO 294-4
Linear Mold Shrinkage, Transverse 0.0080 cm/cm0.0080 in/inISO 294-4
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break 125 MPa18100 psi5mm/min; ISO 527-2/1A
Elongation at Break 1.5 %1.5 %5mm/min; ISO 527-2/1A
Tensile Modulus 11.0 GPa1600 ksi1mm/min; ISO 527-2/1A
Flexural Strength 185 MPa26800 psiISO 178
Flexural Modulus 10.0 GPa1450 ksiISO 178
Izod Impact, Notched (ISO) 6.00 kJ/m²2.86 ft-lb/in²ISO 180/1A
Charpy Impact Unnotched 3.00 J/cm²14.3 ft-lb/in²ISO 179/1eU
Charpy Impact, Notched 0.600 J/cm²2.86 ft-lb/in²ISO 179/1eA
 
Thermal PropertiesMetricEnglishComments
Melting Point 283 °C541 °FISO 11357-1,-2,-3
Deflection Temperature at 1.8 MPa (264 psi) 240 °C464 °FISO 75-1, -2
Flammability, UL94  V-2
@Thickness 0.750 mm
V-2
@Thickness 0.0295 in
 V-0
@Thickness 1.50 mm
V-0
@Thickness 0.0591 in
 
Processing PropertiesMetricEnglishComments
Processing Temperature 95.0 - 120 °C203 - 248 °Fcavity
Melt Temperature 295 - 310 °C563 - 590 °F
Drying Temperature >= 70.0 °C>= 158 °F
Dry Time 4 - 6 hour4 - 6 hour
Moisture Content 0.030 %0.030 %Necessary low maximum

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-39694.html

免责声明: 本文 Celanese Thermx® CG907 PCT, 30% Glass Reinforced 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4