- 密度 [g/cm3]: 1.43
- 缺口冲击强度: 5.0
- 弯曲模量 [MPa]: 7.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 92.0 MPa | 13300 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 1.90 % | 1.90 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 7.50 GPa | 1090 ksi | 1mm/min; ISO 527-2/1A |
| Flexural Strength | 140 MPa | 20300 psi | ISO 178 |
| Flexural Modulus | 7.00 GPa | 1020 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | ISO 180/1A |
| Charpy Impact Unnotched | 3.00 J/cm² | 14.3 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 283 °C | 541 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75-1, -2 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 80.0 - 120 °C | 176 - 248 °F | Cavity temperature |
| Melt Temperature | 295 - 310 °C | 563 - 590 °F | |
| Drying Temperature | >= 95.0 °C | >= 203 °F | |
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour | |
| Moisture Content | 0.0300 % | 0.0300 % | Necessary low maximum residual |