Celanese THERMX CG943 PCT, 40% Glass Reinforced

Celanese THERMX CG943 PCT, 40% Glass Reinforced 物性表: Celanese THERMX CG943 PCT, 40% Glass Reinforced物性表及特性介绍,Celanese THERMX CG943 PCT, 40% Glass Reinforced注塑参数详情,如需Celanese THERMX CG943 PCT, 40% Glass Reinforced下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.7
  • 弯曲模量 [MPa]: 1.285
 
Physical PropertiesMetricEnglishComments
Density 1.70 g/cc0.0614 lb/in³ISO 1183
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break 115 MPa16700 psi5mm/min; ISO 527-2/1A
Elongation at Break 1.30 %1.30 %5mm/min; ISO 527-2/1A
Tensile Modulus 13.0 GPa1890 ksi1mm/min; ISO 527-2/1A
Flexural Strength 178 MPa25800 psiISO 178
Flexural Modulus 1.285 GPa186.4 ksiISO 178
Charpy Impact Unnotched 2.60 J/cm²12.4 ft-lb/in²ISO 179/1eU
Charpy Impact, Notched 0.700 J/cm²3.33 ft-lb/in²ISO 179/1eA
 
Electrical PropertiesMetricEnglishComments
Comparative Tracking Index 380 V380 VIEC 60112
 
Thermal PropertiesMetricEnglishComments
Melting Point 285 °C545 °F10°C/min; ISO 11357-1,-2,-3
Deflection Temperature at 1.8 MPa (264 psi) 262 °C504 °FISO 75-1, -2
Flammability, UL94 V-0
@Thickness 1.60 mm
V-0
@Thickness 0.0630 in
UL94
Oxygen Index 33.0 %33.0 %ISO 4589
 
Processing PropertiesMetricEnglishComments
Processing Temperature 80.0 - 120 °C176 - 248 °FCavity temperature
Melt Temperature 300 °C572 °FOptimum
 295 - 310 °C563 - 590 °F
 295 - 310 °C563 - 590 °F
Mold Temperature 80.0 - 120 °C176 - 248 °F
 100 °C212 °FOptimum
Drying Temperature >= 95.0 °C>= 203 °F
Dry Time 4.00 - 6.00 hour4.00 - 6.00 hour
Moisture Content 0.0300 %0.0300 %Necessary low maximum residual

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-39697.html

免责声明: 本文 Celanese THERMX CG943 PCT, 40% Glass Reinforced 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4