- 熔体流动速率 [g/10min]: 60.0
- 缺口冲击强度: 0.245
- 拉伸强度 [MPa]: 61.8
- 弯曲模量 [MPa]: 6.96
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.60 g/cc | 1.60 g/cc | ASTM D792 |
| Melt Flow | 60 g/10 min @Load 1.20 kg, Temperature 300 °C | 60 g/10 min @Load 2.65 lb, Temperature 572 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 61.8 MPa | 8960 psi | 5 mm/min; ASTM D638 |
| Flexural Strength | 80.4 MPa | 11700 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 6.96 GPa | 1010 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.245 J/cm @Thickness 3.17 mm | 0.459 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 260 °C @Thickness 6.40 mm | 500 °F @Thickness 0.252 in | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.50 - 3.00 mm | HB @Thickness 0.0591 - 0.118 in | |