- 密度 [g/cm3]: 1.57
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.57 g/cc | 0.0567 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.00300 cm/cm | 0.00300 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.00900 cm/cm | 0.00900 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 65.0 MPa | 9430 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 2.00 % | 2.00 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 5.10 GPa | 740 ksi | 1mm/min; ISO 527-2/1A |
| Charpy Impact Unnotched | 3.50 J/cm² | 16.7 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.350 J/cm² | 1.67 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 30.0 µm/m-°C | 16.7 µin/in-°F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 100 µm/m-°C | 55.6 µin/in-°F | ISO 11359-2 |
| Melting Point | 285 °C | 545 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 100 - 150 °C | 212 - 302 °F | Cavity temperature |
| Zone 1 | 290 - 305 °C | 554 - 581 °F | |
| Zone 2 | 285 - 300 °C | 545 - 572 °F | |
| Zone 3 | 285 - 300 °C | 545 - 572 °F | |
| Zone 4 | 285 - 300 °C | 545 - 572 °F | |
| Die Temperature | 285 - 295 °C | 545 - 563 °F | |
| Melt Temperature | 290 - 310 °C | 554 - 590 °F | |
| Drying Temperature | 95.0 - 100 °C | 203 - 212 °F | |
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour | |
| Moisture Content | 0.0300 % | 0.0300 % | Necessary low maximum residual |