- 密度 [g/cm3]: 1.62
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.62 g/cc | 0.0585 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.00300 cm/cm | 0.00300 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.00900 cm/cm | 0.00900 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 73.0 MPa | 10600 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 1.70 % | 1.70 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 6.27 GPa | 909 ksi | 1mm/min; ISO 527-2/1A |
| Charpy Impact Unnotched | 3.20 J/cm² | 15.2 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.320 J/cm² | 1.52 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 32.0 µm/m-°C | 17.8 µin/in-°F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 102 µm/m-°C | 56.7 µin/in-°F | ISO 11359-2 |
| Melting Point | 285 °C | 545 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 100 - 150 °C | 212 - 302 °F | Cavity temperature |
| Zone 1 | 290 - 305 °C | 554 - 581 °F | |
| Zone 2 | 285 - 300 °C | 545 - 572 °F | |
| Zone 3 | 285 - 300 °C | 545 - 572 °F | |
| Zone 4 | 285 - 300 °C | 545 - 572 °F | |
| Die Temperature | 285 - 295 °C | 545 - 563 °F | |
| Melt Temperature | 290 - 310 °C | 554 - 590 °F | |
| Drying Temperature | 95.0 - 100 °C | 203 - 212 °F | |
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour | |
| Moisture Content | 0.0300 % | 0.0300 % | Necessary low maximum residual |