- 密度 [g/cm3]: 1.51
- 弯曲模量 [MPa]: 8.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.51 g/cc | 0.0546 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.00300 cm/cm | 0.00300 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.00900 cm/cm | 0.00900 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 105 MPa | 15200 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 2.30 % | 2.30 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 9.00 GPa | 1310 ksi | 1mm/min; ISO 527-2/1A |
| Flexural Strength | 160 MPa | 23200 psi | ISO 178 |
| Flexural Modulus | 8.00 GPa | 1160 ksi | ISO 178 |
| Charpy Impact Unnotched | 5.50 J/cm² | 26.2 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Dielectric Strength | 38.0 kV/mm | 965 kV/in | IEC 60243-1 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 285 °C | 545 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | ISO 75-1, -2 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 120 - 140 °C | 248 - 284 °F | Cavity temperature |
| Melt Temperature | 295 - 310 °C | 563 - 590 °F | |
| Drying Temperature | 95.0 °C | 203 °F | |
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour | |